Polymer Property : Thermal Conductivity = 117 BTU-in/hr-ftÂ²-Â°F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
Thermal Conductivity	16.9 W/m-K @Temperature 400 Â°C	117 BTU-in/hr-ftÂ²-Â°F @Temperature 752 Â°F
Haynes HastelloyÂ® X alloy, sheet Solid-solution-strengthened with very good high-temperature strength and very good resistance to oxidizing environments up to about 1095Â°C, and good carburization resistance. Applications includ..
Thermal Conductivity	16.8 W/m-K @Temperature 427 Â°C	117 BTU-in/hr-ftÂ²-Â°F @Temperature 801 Â°F
Haynes R-41 alloy, Vacuum melted, exceptionally high strength at temperature between 649-982Â°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ..
Thermal Conductivity	16.8 W/m-K @Temperature 427 Â°C	117 BTU-in/hr-ftÂ²-Â°F @Temperature 801 Â°F
Haynes R-41 alloy, 0.635 mm thick sheet, solution heat treated at 1079Â°C, water quenched, 30 minutes at 1066Â°C, aged 16 hours at 760Â°C (1400Â°F), air cooled Vacuum melted, exceptionally high strength at temperature between 649-982Â°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ..
Thermal Conductivity	16.8 W/m-K @Temperature 427 Â°C	117 BTU-in/hr-ftÂ²-Â°F @Temperature 801 Â°F
Haynes R-41 alloy, 1.27 mm thick sheet, solution heat treated at 1079Â°C, water quenched, 30 minutes at 1066Â°C, aged 16 hours at 760Â°C (1400Â°F), air cooled Vacuum melted, exceptionally high strength at temperature between 649-982Â°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ..
Thermal Conductivity	16.8 W/m-K @Temperature 427 Â°C	117 BTU-in/hr-ftÂ²-Â°F @Temperature 801 Â°F
Haynes R-41 alloy, 1.27 mm thick sheet, solution heat treated at 1079Â°C, water quenched, 30 minutes at 1066Â°C, air cooled, aged 16 hours at 760Â°C (1400Â°F) Vacuum melted, exceptionally high strength at temperature between 649-982Â°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ..
Thermal Conductivity	16.8 W/m-K @Temperature 427 Â°C	117 BTU-in/hr-ftÂ²-Â°F @Temperature 801 Â°F
Haynes R-41 alloy, sheet 0.762-2.54 mm exclusive, 30 minutes at 1066Â°C, air cooled, aged 16 hours at 760Â°C (1400Â°F) Vacuum melted, exceptionally high strength at temperature between 649-982Â°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ..
Thermal Conductivity	16.8 W/m-K @Temperature 427 Â°C	117 BTU-in/hr-ftÂ²-Â°F @Temperature 801 Â°F
Haynes R-41 alloy, sheet 0.762-2.54 mm exclusive, 30 minutes at 1121Â°C, air cooled, aged 16 hours at 899Â°C Vacuum melted, exceptionally high strength at temperature between 649-982Â°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ..
Thermal Conductivity	16.9 W/m-K @Temperature 400 Â°C	117 BTU-in/hr-ftÂ²-Â°F @Temperature 752 Â°F
Haynes X-750 Nickel Alloy Sheet and Strip (AMS 5598, UNS N07750) Haynes X-750 (UNS No. N07750) alloy is an age-hardenable, nickel-base superalloy with very good strength at temperatures up to about 1600Â°F (870Â°C). It is widely used as a wrought material for..
Thermal Conductivity	16.9 W/m-K @Temperature 600 °C	117 BTU-in/hr-ft²-°F @Temperature 1110 °F	Hardened Condition
Bohler-Uddeholm BÖHLER W302 SUPERIOR® Premium H13 Tool Steel A premium grade H13 hot work tool steel featuring:Very good toughness properties meeting the requirements of NADCA 207-97, and the superior quality levels of NADCA 207-2003Very good heat checking re..
Thermal Conductivity	16.8 W/m-K @Temperature 427 °C	117 BTU-in/hr-ft²-°F @Temperature 801 °F
Haynes R-41 alloy, Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications include ..