Thermal Properties | Metric | English | Comments |
---|---|---|---|
Maximum Service Temperature, Air | 649 °C | 1200 °F | |
Palm Labs Adhesives Turbo Anti-Seize Copper Paste TURBO ANTI-SEIZE – COPPER is a copper, viscous metallic paste which may be used on all bolts, studs, value shafts, value assemblies, transmission shafts, and other types of assembly work where prot.. |
|||
Maximum Service Temperature, Air | 649 °C | 1200 °F | |
Palm Labs Adhesives Turbo Anti-Seize Nickel Paste TURBO ANTI-SEIZE – NICKEL is a gray, viscous metallic paste which may be used on all bolts, studs, value shafts, value assemblies, transmission shafts, and other types of assembly work where protec.. |
|||
Maximum Service Temperature, Air | 650 °C | 1200 °F | |
Pyrotek G-1 Low-Temperature Felt An inexpensive, tough material. Will not support combustion.Rolls:610 mm x 30.5 m 13 & 25 mm thickApplicationsHigh-temperature gasketsInformation provided by Pyrotek. |
|||
Maximum Service Temperature, Air | 650 °C | 1200 °F | |
Pyrotek G-2 Low-Temperature Felt An inexpensive tough material.Dimensions610 mm x 30.5 m 25 mm thickApplicationsHigh-temperature gasketsInformation provided by Pyrotek. |
|||
Maximum Service Temperature, Air | 650 °C | 1200 °F | Continuous |
Pyrotek IR-3 Fiber Seal Pre-cut Gasket A felt-like material which expands between 350°C and 540°C.Information provided by Pyrotek. |
|||
Maximum Service Temperature, Air | 650 °C | 1200 °F | |
Pyrotek IR-3 Low-Temperature Felt Felt-like material which expands between 350°C and 540°C.Custom Rolls:3 & 6 mm thickApplicationsCompressible gasketing Collector bar seals Siphon gaskets Flange gaskets Information provided by Pyr.. |
|||
Maximum Service Temperature, Air | 650 °C | 1200 °F | Continuous |
Pyrotek O1-C Fiber Seal Pre-cut Gasket Silicone coated felt. Excellent resistance to vibration. Coating burns off at 315°C.Information provided by Pyrotek. |
|||
Maximum Service Temperature, Air | 650 °C | 1200 °F | for Continuous use with standard cloth exterior |
Pyrotek MT-29L Microporous Ladle Lining Insulation MT-29L is a microporous insulation material covered with a flexible glass fabric. Parallel-stitched for ease of handling during installation, it is designed for use between ladle shells and the bac.. |
|||
Maximum Service Temperature, Air | 649 °C | 1200 °F | Steam |
Garlock GRAPH-LOCK® 3124/3126 Graphite Sheet Gasketing, Steel Wire Insert A laminated graphite sheet with a 316SS wire mesh insert.Pure exfoliated graphite flake material excels in extreme conditions, withstanding heat, pressure, and aggressive chemicalsProven fire-safeSe.. |
|||
Maximum Service Temperature, Air | 649 °C | 1200 °F | Steam |
Garlock GRAPH-LOCK® 3125SS Graphite Sheet Gasketing, Steel Foil Insert A laminated graphite sheet with a 316SS foil insert.Pure exfoliated graphite flake material excels in extreme conditions, withstanding heat, pressure, and aggressive chemicalsProven fire-safeSeals e.. |
|||
Maximum Service Temperature, Air | 650 °C | 1200 °F | for long term exposure |
Microtherm Group MT Thermosphere® Moldable Insulation Paste MT Thermosphere® is a low density temperature resistant paste with excellent thermal insulation properties from cryogenic to high temperature exposure. It is a perfectly seamless insulation syste.. |
|||
Maximum Service Temperature, Air | 649 °C | 1200 °F | Upper limit of working range |
Heatbath/Park Alu-Braze 860 Aluminum Brazing Salt This is our premium aluminum dip braze salt. By proper chemical balance the lowest practical melt point has been developed with no sacrifices in fluidity or braze characteristics. Because of its sig.. |
|||
Maximum Service Temperature, Air | 649 °C | 1200 °F | Upper limit of working range |
Heatbath/Park Alu-Braze 930 Aluminum Brazing Salt An improved salt having similar compositions but improved braze characteristics compared to Alu-Braze 960. The lower melt point offers good fluidity over a wider temperature and is ideally suited fo.. |
|||
Maximum Service Temperature, Air | 649 °C | 1200 °F | Upper limit of working range |
Heatbath/Park Alu-Braze 960 Aluminum Brazing Salt This is the standard salt designed for low melting point, good fluidity, and good braze characteristics.Information provided by Heatbath Corporation - Park Metallurgical. |
|||
Maximum Service Temperature, Air | 650 °C | 1200 °F | resistance to low cycle and thermal fatigue |
Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed + 10% Cold Work Tensile strength (ultimate and yield), elongation, and reduction of area values are for annealed then cold worked samples. This produces ASTM grain size 9.0. Other property values are typical of t.. |
|||
Maximum Service Temperature, Air | 650 °C | 1200 °F | resistance to low cycle and thermal fatigue |
Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed + 5% Cold Work Tensile strength (ultimate and yield), elongation, and reduction of area values are for annealed then cold worked samples. This produces ASTM grain size 9.0. Other property values are typical of t.. |
|||
Maximum Service Temperature, Air | 650 °C | 1200 °F | resistance to low cycle and thermal fatigue |
Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed + 50% Cold Work Tensile strength (ultimate and yield), elongation, and reduction of area values are for annealed then cold worked samples. This produces ASTM grain size 10.0. Other property values are typical of .. |
|||
Maximum Service Temperature, Air | 650 °C | 1200 °F | resistance to low cycle and thermal fatigue |
Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed 1950°F (1070°C) + Aged 1400°F (760°C) Tensile strength (ultimate and yield), elongation, and hardness values are for samples annealed 1950°F (1070°C)/5 minutes/AC + Aged 1400°F (760°C)/100h/AC. This produces ASTM grain siz.. |
|||
Maximum Service Temperature, Air | 650 °C | 1200 °F | resistance to low cycle and thermal fatigue |
Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed 2150°F (1180°C) + Aged 1400°F (760°C) Tensile strength (ultimate and yield), elongation, and hardness values are for samples annealed 2150°F (1180°C)/5 minutes/AC + Aged 1400°F (760°C)/100h/AC. This produces ASTM grain siz.. |
|||
Maximum Service Temperature, Air | 650 °C | 1200 °F | Normal atmosphere |
Sinotek Materials Tungsten Disulfide (WS2) Powder, High-Purity Tungsten Disulfide powder mainly has applications in spraying, coating, carbon material, all sorts of grease, lubricating oil, friction materials and catalysts. Tungsten Disulfide has good resistan.. |
|||
Maximum Service Temperature, Air | 649 °C | 1200 °F | |
Dura-Bar 80-55-06 Continuously Cast Ductile Iron Bar Stock ASTM A536 Continuously cast ductile iron bar stock is produced in a wide variety of sizes and shapes, including rounds, rectangles and special shape cross sections.It often is used as a direct replacement for.. |
|||
Maximum Service Temperature, Air | 650 °C | 1200 °F | in normal atmosphere |
BryCoat WS2 Tungsten Disulfide Coating WS2's unique, extensively modified lamellar composition of tungsten disulfide results in a high performance dry coating lubricant. A pressurized air application processes impinges a dry metallic co.. |
|||
Maximum Service Temperature, Air | 649 °C | 1200 °F | |
Aremco Ceramabind™ 880 High Temperature Inorganic Binder High Temperature, water-dispersible silicone resin for producing corrosion and moisture resistant coatings and sealing porous ceramics. Cures at 450 °F in one hour. |
|||
Maximum Service Temperature, Air | 650 °C | 1200 °F | Continuous |
Pyrotek G-1 Fiber Seal Pre-cut Gasket A black, inexpensive material. Will not support combustion.Information provided by Pyrotek. |
|||
Maximum Service Temperature, Air | 650 °C | 1200 °F | |
Pyrotek O-1 Low-Temperature Felt Excellent resistance to vibration. Not effected by 1.55 MPa steam.Dimensions1524 mm x 22.9 m 6, 13, 25 mm thickApplicationsHigh-density gaskets at elevated temperatures Initial systems, high pressu.. |