- Polymer Property : Thermal Conductivity = 99.2 BTU-in/hr-ft²-°F
Polymer Property : Thermal Conductivity = 99.2 BTU-in/hr-ft²-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 14.3 W/m-K @Temperature 200 °C |
99.2 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 188 alloy, 0% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Thermal Conductivity | 14.3 W/m-K @Temperature 200 °C |
99.2 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Thermal Conductivity | 14.3 W/m-K @Temperature 200 °C |
99.2 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Thermal Conductivity | 14.3 W/m-K @Temperature 200 °C |
99.2 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Thermal Conductivity | 14.3 W/m-K @Temperature 200 °C |
99.2 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Thermal Conductivity | 14.3 W/m-K @Temperature 200 °C |
99.2 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Thermal Conductivity | 14.3 W/m-K @Temperature 200 °C |
99.2 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Thermal Conductivity | 14.3 W/m-K @Temperature 200 °C |
99.2 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Thermal Conductivity | 14.3 W/m-K @Temperature 200 °C |
99.2 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Thermal Conductivity | 14.3 W/m-K @Temperature 200 °C |
99.2 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Thermal Conductivity | 14.3 W/m-K @Temperature 200 °C |
99.2 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Thermal Conductivity | 14.3 W/m-K @Temperature 200 °C |
99.2 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Thermal Conductivity | 14.3 W/m-K @Temperature 200 °C |
99.2 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Thermal Conductivity | 14.3 W/m-K @Temperature 200 °C |
99.2 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Thermal Conductivity | 14.3 W/m-K @Temperature 200 °C |
99.2 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 188 alloy, plate at RT after 0 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Thermal Conductivity | 14.3 W/m-K @Temperature 200 °C |
99.2 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 188 alloy, plate at RT after 1000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Thermal Conductivity | 14.3 W/m-K @Temperature 200 °C |
99.2 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 188 alloy, plate at RT after 16000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Thermal Conductivity | 14.3 W/m-K @Temperature 200 °C |
99.2 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 188 alloy, plate at RT after 4000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Thermal Conductivity | 14.3 W/m-K @Temperature 200 °C |
99.2 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 188 alloy, plate at RT after 8000 hours at 650°C (1200°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Thermal Conductivity | 14.3 W/m-K @Temperature 200 °C |
99.2 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 188 alloy, plate at RT after 8000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Thermal Conductivity | 14.3 W/m-K @Temperature 200 °C |
99.2 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes HR-120® alloy, solution heat-treated Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
| Thermal Conductivity | 14.3 W/m-K @Temperature 200 °C |
99.2 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes HR-120® alloy, solution heat-treated aged at 1200°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
| Thermal Conductivity | 14.3 W/m-K @Temperature 200 °C |
99.2 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes HR-120® alloy, solution heat-treated aged at 1400°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
| Thermal Conductivity | 14.3 W/m-K @Temperature 200 °C |
99.2 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes HR-120® alloy, solution heat-treated aged at 1600°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
| Thermal Conductivity | 14.3 W/m-K @Temperature 200 °C |
99.2 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes HR-120® alloy, solution heat-treated aged at 1800°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
| Thermal Conductivity | 14.3 W/m-K @Temperature 200 °C |
99.2 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Thermal Conductivity | 14.3 W/m-K @Temperature 200 °C |
99.2 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Thermal Conductivity | 14.3 W/m-K @Temperature 200 °C |
99.2 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 188 alloy, plate at RT after 8000 hours at 760°C (1400°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Thermal Conductivity | 14.3 W/m-K @Temperature 200 °C |
99.2 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 718 alloy, cold rolled, solution-treated and aged sheet Cb and Ta content combined weight percentage of 5. Excellent high-temperature strength up to 650°C, good ductility, formability, and weldability. Very good welding characteristics. Applications i.. |
|||
| Thermal Conductivity | 14.3 W/m-K | 99.2 BTU-in/hr-ft²-°F | RT |
| Outokumpu 4948 High Temperature Austenitic Stainless Steel Creep-resistant variant of 1.4301, with a standardized minimum carbon content for service at temperatures of up to 800°C in dry air.Applications: Heat and creep resistance. For use over 550°C for.. |
|||