Polymer Property : Thermal Conductivity = 26.9 W/m-K Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
Thermal Conductivity	26.9 W/m-K @Temperature 700 Â°C	187 BTU-in/hr-ftÂ²-Â°F @Temperature 1290 Â°F
Haynes 214Â® alloy sheet Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity	26.9 W/m-K @Temperature 700 Â°C	187 BTU-in/hr-ftÂ²-Â°F @Temperature 1290 Â°F
Haynes 214Â® alloy, 0% cold reduction Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity	26.9 W/m-K @Temperature 700 Â°C	187 BTU-in/hr-ftÂ²-Â°F @Temperature 1290 Â°F
Haynes 214Â® alloy, 10% cold reduction Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity	26.9 W/m-K @Temperature 700 Â°C	187 BTU-in/hr-ftÂ²-Â°F @Temperature 1290 Â°F
Haynes 214Â® alloy, 10% cold reduction, 980Â°C (1800Â°F) for 5 minutes Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity	26.9 W/m-K @Temperature 700 Â°C	187 BTU-in/hr-ftÂ²-Â°F @Temperature 1290 Â°F
Haynes 214Â® alloy, 20% cold reduction Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity	26.9 W/m-K @Temperature 700 Â°C	187 BTU-in/hr-ftÂ²-Â°F @Temperature 1290 Â°F
Haynes 214Â® alloy, 20% cold reduction, 925Â°C for 5 minutes Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity	26.9 W/m-K @Temperature 700 Â°C	187 BTU-in/hr-ftÂ²-Â°F @Temperature 1290 Â°F
Haynes 214Â® alloy, 30% cold reduction, 1095Â°C (2000Â°F) for 5 minutes Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity	26.9 W/m-K @Temperature 700 Â°C	187 BTU-in/hr-ftÂ²-Â°F @Temperature 1290 Â°F
Haynes 214Â® alloy, 30% cold reduction, 925Â°C for 5 minutes Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity	26.9 W/m-K @Temperature 700 Â°C	187 BTU-in/hr-ftÂ²-Â°F @Temperature 1290 Â°F
Haynes 214Â® alloy, 40% cold reduction Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity	26.9 W/m-K @Temperature 700 Â°C	187 BTU-in/hr-ftÂ²-Â°F @Temperature 1290 Â°F
Haynes 214Â® alloy, 40% cold reduction, 1095Â°C (2000Â°F) for 5 minutes Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity	26.9 W/m-K @Temperature 700 Â°C	187 BTU-in/hr-ftÂ²-Â°F @Temperature 1290 Â°F
Haynes 214Â® alloy, 40% cold reduction, 925Â°C for 5 minutes Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity	26.9 W/m-K @Temperature 700 Â°C	187 BTU-in/hr-ftÂ²-Â°F @Temperature 1290 Â°F
Haynes 214Â® alloy, 50% cold reduction Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity	26.9 W/m-K @Temperature 700 Â°C	187 BTU-in/hr-ftÂ²-Â°F @Temperature 1290 Â°F
Haynes 214Â® alloy, 50% cold reduction, 1095Â°C (2000Â°F) for 5 minutes Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity	26.9 W/m-K @Temperature 700 Â°C	187 BTU-in/hr-ftÂ²-Â°F @Temperature 1290 Â°F
Haynes 214Â® alloy, 50% cold reduction, 980Â°C (1800Â°F) for 5 minutes Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity	26.9 W/m-K @Temperature 700 Â°C	187 BTU-in/hr-ftÂ²-Â°F @Temperature 1290 Â°F
Haynes 214Â® alloy, sheet, 100 hours exposure at 760Â°C (1400Â°F) Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity	26.9 W/m-K @Temperature 700 Â°C	187 BTU-in/hr-ftÂ²-Â°F @Temperature 1290 Â°F
Haynes 214Â® alloy, sheet, 100 hours exposure at 980Â°C (1800Â°F) Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity	26.9 W/m-K @Temperature 700 Â°C	187 BTU-in/hr-ftÂ²-Â°F @Temperature 1290 Â°F
Haynes 214Â® alloy, sheet, 1000 hours exposure at 760Â°C (1400Â°F) Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity	26.9 W/m-K @Temperature 700 Â°C	187 BTU-in/hr-ftÂ²-Â°F @Temperature 1290 Â°F
Haynes 214Â® alloy, sheet, 1000 hours exposure at 980Â°C (1800Â°F) Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity	26.9 W/m-K @Temperature 700 Â°C	187 BTU-in/hr-ftÂ²-Â°F @Temperature 1290 Â°F
Haynes 214Â® alloy, sheet, 32 hours exposure at 870Â°C (1600Â°F) Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity	26.9 W/m-K @Temperature 700 Â°C	187 BTU-in/hr-ftÂ²-Â°F @Temperature 1290 Â°F
Haynes 214Â® alloy, sheet, 32 hours exposure at 980Â°C (1800Â°F) Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity	26.9 W/m-K @Temperature 900 Â°C	187 BTU-in/hr-ftÂ²-Â°F @Temperature 1650 Â°F
Haynes HR-160Â® alloy plate, aged 4000 hours at 649Â°C (1200Â°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Thermal Conductivity	26.9 W/m-K @Temperature 900 Â°C	187 BTU-in/hr-ftÂ²-Â°F @Temperature 1650 Â°F
Haynes HR-160Â® alloy, plate, aged 1000 hours at 760Â°C (1400Â°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Thermal Conductivity	26.9 W/m-K @Temperature 900 Â°C	187 BTU-in/hr-ftÂ²-Â°F @Temperature 1650 Â°F
Haynes HR-160Â® alloy, plate, aged 4000 hours at 871Â°C (1600Â°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Thermal Conductivity	26.9 W/m-K @Temperature 900 Â°C	187 BTU-in/hr-ftÂ²-Â°F @Temperature 1650 Â°F
Haynes HR-160Â® alloy, plate, aged 8000 hours at 760Â°C (1400Â°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Thermal Conductivity	26.9 W/m-K @Temperature 900 Â°C	187 BTU-in/hr-ftÂ²-Â°F @Temperature 1650 Â°F
Haynes HR-160Â® alloy, plate, aged 8000 hours at 871Â°C (1600Â°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Thermal Conductivity	26.9 W/m-K @Temperature 700 Â°C	187 BTU-in/hr-ftÂ²-Â°F @Temperature 1290 Â°F
Haynes 214Â® alloy, 10% cold reduction, 1095Â°C (2000Â°F) for 5 minutes Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Thermal Conductivity	26.9 W/m-K @Temperature 900 Â°C	187 BTU-in/hr-ftÂ²-Â°F @Temperature 1650 Â°F
Haynes HR-160Â® alloy plate, aged 8000 hours at 649Â°C (1200Â°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Thermal Conductivity	26.9 W/m-K @Temperature 100 °C	187 BTU-in/hr-ft²-°F @Temperature 212 °F	ASTM-C408
CoorsTek Superstrate® 996 99.6% Alumina Thin Film Applications: thin film substrates
Thermal Conductivity	26.9 W/m-K @Temperature 100 °C	187 BTU-in/hr-ft²-°F @Temperature 212 °F
AK Steel 410S Ferritic Stainless steel AK Steel 410S Stainless Steel is a non-hardening modification of Type 410. A small titanium addition minimizes austenite formation at high temperatures, thereby restricting the alloy's ability to h..
Thermal Conductivity	26.9 W/m-K	187 BTU-in/hr-ft²-°F
ATI Allegheny Ludlum Stainless Steel AL 410S™ (UNS S41008) Allegheny Ludlum Al 410S™ stainless steel is a low-carbon modification of Type 410 stainless steel. Low carbon and optionally a small addition of titanium and /or columbium minimize austenite form..