- Polymer Property : Thermal Conductivity = 21.5 W/m-K
Polymer Property : Thermal Conductivity = 21.5 W/m-K Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 21.5 W/m-K @Temperature 800 °C |
149 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, 0% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 21.5 W/m-K @Temperature 800 °C |
149 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, 10% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 21.5 W/m-K @Temperature 800 °C |
149 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, 20% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 21.5 W/m-K @Temperature 800 °C |
149 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, 20% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 21.5 W/m-K @Temperature 800 °C |
149 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, 20% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 21.5 W/m-K @Temperature 800 °C |
149 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, 20% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 21.5 W/m-K @Temperature 800 °C |
149 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 21.5 W/m-K @Temperature 800 °C |
149 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 21.5 W/m-K @Temperature 800 °C |
149 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 21.5 W/m-K @Temperature 800 °C |
149 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, 40% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 21.5 W/m-K @Temperature 800 °C |
149 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, 40% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 21.5 W/m-K @Temperature 800 °C |
149 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, 40% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 21.5 W/m-K @Temperature 800 °C |
149 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, 50% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 21.5 W/m-K @Temperature 800 °C |
149 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, 50% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 21.5 W/m-K @Temperature 800 °C |
149 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, plate after 1000 hours at 650°C (1200°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 21.5 W/m-K @Temperature 800 °C |
149 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, plate after 16000 hours at 650°C (1200°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 21.5 W/m-K @Temperature 800 °C |
149 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, plate after 16000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 21.5 W/m-K @Temperature 800 °C |
149 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, plate after 4000 hours at 650°C (1200°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 21.5 W/m-K @Temperature 800 °C |
149 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, plate after 4000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 21.5 W/m-K @Temperature 800 °C |
149 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, plate after 8000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 21.5 W/m-K @Temperature 800 °C |
149 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, plate after 8000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 21.5 W/m-K @Temperature 800 °C |
149 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, plate, as annealed at 1025°C, rapid cooled Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Thermal Conductivity | 21.5 W/m-K | 149 BTU-in/hr-ft²-°F | |
| ATI Wah Chang Zirconium Alloy Zircaloy-4 Zirconium resists corrosive attack in most organic and mineral acids, strong alkalis, and some molten salts. A tightly adherent and protective oxide film protects the metal-oxide interface to provid.. |
|||
| Thermal Conductivity | 21.5 W/m-K @Temperature 800 °C |
149 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, 30% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Thermal Conductivity | 21.5 W/m-K @Temperature 800 °C |
149 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Thermal Conductivity | 21.5 W/m-K @Temperature 800 °C |
149 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, 40% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Thermal Conductivity | 21.5 W/m-K @Temperature 800 °C |
149 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, 50% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Thermal Conductivity | 21.5 W/m-K @Temperature 800 °C |
149 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, 10% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C (1500°F), good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a var.. |
|||
| Thermal Conductivity | 21.5 W/m-K @Temperature 800 °C |
149 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, 10% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Thermal Conductivity | 21.5 W/m-K @Temperature 800 °C |
149 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 625 alloy, 40% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||