ATI Wah Chang Zirconium Alloy Zircaloy-4
| Category | Metal , Nonferrous Metal , Zirconium Alloy |
| Manufacturer | ATI Wah Chang |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ATI Wah Chang Zirconium Alloy Zircaloy-4.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Zirconium resists corrosive attack in most organic and mineral acids, strong alkalis, and some molten salts. A tightly adherent and protective oxide film protects the metal-oxide interface to provide corrosion resistance. An additional benefit for zirconium alloys in long-term geological disposal options is the inert nature of zirconium oxide.Information provided by ATI Wah Chang
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 6.56 g/cc | 0.237 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell B | 89 | 89 | |
| Tensile Strength, Ultimate | 241 MPa @Temperature 288 °C |
34900 psi @Temperature 550 °F |
Transverse |
| 271 MPa @Temperature 288 °C |
39300 psi @Temperature 550 °F |
Longitudinal | |
| 514 MPa @Temperature 23.0 °C |
74600 psi @Temperature 73.4 °F |
||
| 541 MPa @Temperature 23.0 °C |
78400 psi @Temperature 73.4 °F |
||
| Tensile Strength, Yield | 152 MPa @Temperature 288 °C |
22000 psi @Temperature 550 °F |
Longitudinal |
| 177 MPa @Temperature 288 °C |
25600 psi @Temperature 550 °F |
Transverse | |
| 381 MPa @Temperature 23.0 °C |
55200 psi @Temperature 73.4 °F |
||
| 467 MPa @Temperature 23.0 °C |
67800 psi @Temperature 73.4 °F |
||
| Modulus of Elasticity | 99.3 GPa | 14400 ksi | |
| Poissons Ratio | 0.37 | 0.37 | |
| Shear Modulus | 36.19 GPa | 5249 ksi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 6.00 µm/m-°C @Temperature 20.0 °C |
3.33 µin/in-°F @Temperature 68.0 °F |
|
| Thermal Conductivity | 21.5 W/m-K | 149 BTU-in/hr-ft²-°F | |
| Melting Point | 1850 °C | 3360 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Chromium, Cr | 0.070 - 0.13 % | 0.070 - 0.13 % | |
| Fe + Cr | 0.28 - 0.37 % | 0.28 - 0.37 % | |
| Iron, Fe | 0.18 - 0.24 % | 0.18 - 0.24 % | |
| Tin, Sn | 1.2 - 1.7 % | 1.2 - 1.7 % | |
| Zirconium, Zr | 97.56 - 98.27 % | 97.56 - 98.27 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Alpha + Beta -> Beta Phase Transformation | 980°C | |
| Alpha -> Alpha + Beta Phase Transformation | 810°C |