Polymer Property : Thermal Conductivity = 20.6 W/m-K Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English
Thermal Conductivity	20.6 W/m-K @Temperature 600 Â°C	143 BTU-in/hr-ftÂ²-Â°F @Temperature 1110 Â°F
Haynes HR-120Â® alloy, solution heat-treated Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts ..
Thermal Conductivity	20.6 W/m-K @Temperature 600 Â°C	143 BTU-in/hr-ftÂ²-Â°F @Temperature 1110 Â°F
Haynes HR-120Â® alloy, solution heat-treated aged at 1200Â°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts ..
Thermal Conductivity	20.6 W/m-K @Temperature 600 Â°C	143 BTU-in/hr-ftÂ²-Â°F @Temperature 1110 Â°F
Haynes HR-120Â® alloy, solution heat-treated aged at 1400Â°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts ..
Thermal Conductivity	20.6 W/m-K @Temperature 600 Â°C	143 BTU-in/hr-ftÂ²-Â°F @Temperature 1110 Â°F
Haynes HR-120Â® alloy, solution heat-treated aged at 1600Â°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts ..
Thermal Conductivity	20.6 W/m-K @Temperature 600 Â°C	143 BTU-in/hr-ftÂ²-Â°F @Temperature 1110 Â°F
Haynes HR-120Â® alloy, solution heat-treated aged at 1800Â°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts ..
Thermal Conductivity	20.6 W/m-K @Temperature 600 Â°C	143 BTU-in/hr-ftÂ²-Â°F @Temperature 1110 Â°F
Haynes 718 alloy, cold rolled, solution-treated and aged sheet Cb and Ta content combined weight percentage of 5. Excellent high-temperature strength up to 650Â°C, good ductility, formability, and weldability. Very good welding characteristics. Applications i..