- Polymer Property : Thermal Conductivity = 169 BTU-in/hr-ft²-°F
Polymer Property : Thermal Conductivity = 169 BTU-in/hr-ft²-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 24.4 W/m-K @Temperature 800 °C |
169 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 230® alloy plate Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 24.4 W/m-K @Temperature 800 °C |
169 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 230® alloy plate, 1000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 24.4 W/m-K @Temperature 800 °C |
169 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 230® alloy plate, 4000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 24.4 W/m-K @Temperature 800 °C |
169 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 230® alloy, 0% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 24.4 W/m-K @Temperature 800 °C |
169 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 230® alloy, 10% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 24.4 W/m-K @Temperature 800 °C |
169 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 230® alloy, 10% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 24.4 W/m-K @Temperature 800 °C |
169 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 230® alloy, 20% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 24.4 W/m-K @Temperature 800 °C |
169 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 230® alloy, 20% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 24.4 W/m-K @Temperature 800 °C |
169 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 230® alloy, 20% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 24.4 W/m-K @Temperature 800 °C |
169 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 230® alloy, 20% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 24.4 W/m-K @Temperature 800 °C |
169 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 230® alloy, 30% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 24.4 W/m-K @Temperature 800 °C |
169 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 230® alloy, 30% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 24.4 W/m-K @Temperature 800 °C |
169 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 230® alloy, 30% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 24.4 W/m-K @Temperature 800 °C |
169 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 230® alloy, 40% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 24.4 W/m-K @Temperature 800 °C |
169 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 230® alloy, 40% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 24.4 W/m-K @Temperature 800 °C |
169 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 230® alloy, 40% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 24.4 W/m-K @Temperature 800 °C |
169 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 230® alloy, plate, 1000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 24.4 W/m-K @Temperature 800 °C |
169 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 230® alloy, plate, 4000 hours exposure at 760°C (1400°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 24.3 W/m-K @Temperature 20.0 °C |
169 BTU-in/hr-ft²-°F @Temperature 68.0 °F |
|
| Industeel CLC 1.2316 Prehardened (300HB) and Corrosion Resistant Mold Steel Description: CLC 1.2316 is a 16%Cr 1% Mo with improved corrosion resistance properties, thanks to the chromium/molybdenum additions. The high cleanliness/homogeneity of the steel makes it specially .. |
|||
| Thermal Conductivity | 24.3 W/m-K @Temperature 20.0 °C |
169 BTU-in/hr-ft²-°F @Temperature 68.0 °F |
|
| Industeel CLC 1.2316S Prehardened Mold Steel (300HB) with Improved Machinability Description: CLC 1.2316 S grade is a 16%Cr 1%Mo mold steel with improved corrosion resistance properties, thanks to the chromium and molybdenum additions. Furthermore specific sulfur additions are c.. |
|||
| Thermal Conductivity | 24.4 W/m-K @Temperature 800 °C |
169 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 230® alloy, plate, 8000 hours exposure at 760°C (1400°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 24.4 W/m-K @Temperature 800 °C |
169 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 230® alloy, plate, 8000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Thermal Conductivity | 24.4 W/m-K @Temperature 800 °C |
169 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 230® alloy, plate, 1000 hours exposure at 760°C (1400°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| Thermal Conductivity | 24.4 W/m-K @Temperature 800 °C |
169 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 230® alloy, plate, 16000 hours exposure at 760°C (1400°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| Thermal Conductivity | 24.4 W/m-K @Temperature 800 °C |
169 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 230® alloy, plate, 16000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| Thermal Conductivity | 24.4 W/m-K @Temperature 800 °C |
169 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 230® alloy plate, 16000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| Thermal Conductivity | 24.4 W/m-K @Temperature 800 °C |
169 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 230® alloy plate, 8000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| Thermal Conductivity | 24.4 W/m-K @Temperature 800 °C |
169 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 230® alloy, 50% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| Thermal Conductivity | 24.4 W/m-K @Temperature 800 °C |
169 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 230® alloy, 50% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| Thermal Conductivity | 24.4 W/m-K @Temperature 800 °C |
169 BTU-in/hr-ft²-°F @Temperature 1470 °F |
|
| Haynes 230® alloy, plate, 4000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||