Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 18.2 µm/m-°C @Temperature 20.0 - 300 °C |
10.1 µin/in-°F @Temperature 68.0 - 572 °F |
|
Eagle Brass 519 Phosphor Bronzes 6%, 1/2 Hard Alloy C519 has 6% nominal tin producing higher mechanical strengths with a slight decrease in electrical conductivity when compared to C510 phosphor bronze. Often functionally interchangeable with C.. |
|||
CTE, linear | 18.2 µm/m-°C @Temperature 20.0 - 300 °C |
10.1 µin/in-°F @Temperature 68.0 - 572 °F |
|
Eagle Brass 519 Phosphor Bronzes 6%, 1/4 Hard Alloy C519 has 6% nominal tin producing higher mechanical strengths with a slight decrease in electrical conductivity when compared to C510 phosphor bronze. Often functionally interchangeable with C.. |
|||
CTE, linear | 18.2 µm/m-°C @Temperature 20.0 - 300 °C |
10.1 µin/in-°F @Temperature 68.0 - 572 °F |
|
Eagle Brass 519 Phosphor Bronzes 6%, 3/4 Hard Alloy C519 has 6% nominal tin producing higher mechanical strengths with a slight decrease in electrical conductivity when compared to C510 phosphor bronze. Often functionally interchangeable with C.. |
|||
CTE, linear | 18.2 µm/m-°C @Temperature 20.0 - 300 °C |
10.1 µin/in-°F @Temperature 68.0 - 572 °F |
|
Eagle Brass 519 Phosphor Bronzes 6%, Annealed Alloy C519 has 6% nominal tin producing higher mechanical strengths with a slight decrease in electrical conductivity when compared to C510 phosphor bronze. Often functionally interchangeable with C.. |
|||
CTE, linear | 18.2 µm/m-°C @Temperature 20.0 - 300 °C |
10.1 µin/in-°F @Temperature 68.0 - 572 °F |
|
Eagle Brass 519 Phosphor Bronzes 6%, Extra Hard Alloy C519 has 6% nominal tin producing higher mechanical strengths with a slight decrease in electrical conductivity when compared to C510 phosphor bronze. Often functionally interchangeable with C.. |
|||
CTE, linear | 18.2 µm/m-°C @Temperature 20.0 - 300 °C |
10.1 µin/in-°F @Temperature 68.0 - 572 °F |
|
Eagle Brass 519 Phosphor Bronzes 6%, Extra Spring Alloy C519 has 6% nominal tin producing higher mechanical strengths with a slight decrease in electrical conductivity when compared to C510 phosphor bronze. Often functionally interchangeable with C.. |
|||
CTE, linear | 18.2 µm/m-°C @Temperature 20.0 - 300 °C |
10.1 µin/in-°F @Temperature 68.0 - 572 °F |
|
Eagle Brass 519 Phosphor Bronzes 6%, Hard Alloy C519 has 6% nominal tin producing higher mechanical strengths with a slight decrease in electrical conductivity when compared to C510 phosphor bronze. Often functionally interchangeable with C.. |
|||
CTE, linear | 18.2 µm/m-°C @Temperature 20.0 - 300 °C |
10.1 µin/in-°F @Temperature 68.0 - 572 °F |
|
Eagle Brass 519 Phosphor Bronzes 6%, Spring Alloy C519 has 6% nominal tin producing higher mechanical strengths with a slight decrease in electrical conductivity when compared to C510 phosphor bronze. Often functionally interchangeable with C.. |
|||
CTE, linear | 18.2 µm/m-°C @Temperature 20.0 - 300 °C |
10.1 µin/in-°F @Temperature 68.0 - 572 °F |
|
Eagle Brass 521 Phosphor Bronzes 8% C, 1/2 Hard Alloy C521 is a high tin alloy of the phosphor bronze family. The additional tin relative to the more commonly used C510 results in higher mechanical properties with a modest reduction in electrical.. |
|||
CTE, linear | 18.2 µm/m-°C @Temperature 20.0 - 300 °C |
10.1 µin/in-°F @Temperature 68.0 - 572 °F |
|
Eagle Brass 521 Phosphor Bronzes 8% C, 1/4 Hard Alloy C521 is a high tin alloy of the phosphor bronze family. The additional tin relative to the more commonly used C510 results in higher mechanical properties with a modest reduction in electrical.. |
|||
CTE, linear | 18.2 µm/m-°C @Temperature 20.0 - 300 °C |
10.1 µin/in-°F @Temperature 68.0 - 572 °F |
|
Eagle Brass 521 Phosphor Bronzes 8% C, 3/4 Hard Alloy C521 is a high tin alloy of the phosphor bronze family. The additional tin relative to the more commonly used C510 results in higher mechanical properties with a modest reduction in electrical.. |
|||
CTE, linear | 18.2 µm/m-°C @Temperature 20.0 - 300 °C |
10.1 µin/in-°F @Temperature 68.0 - 572 °F |
|
Eagle Brass 521 Phosphor Bronzes 8% C, Annealed Alloy C521 is a high tin alloy of the phosphor bronze family. The additional tin relative to the more commonly used C510 results in higher mechanical properties with a modest reduction in electrical.. |
|||
CTE, linear | 18.2 µm/m-°C @Temperature 20.0 - 300 °C |
10.1 µin/in-°F @Temperature 68.0 - 572 °F |
|
Eagle Brass 521 Phosphor Bronzes 8% C, Extra Hard Alloy C521 is a high tin alloy of the phosphor bronze family. The additional tin relative to the more commonly used C510 results in higher mechanical properties with a modest reduction in electrical.. |
|||
CTE, linear | 18.2 µm/m-°C @Temperature 20.0 - 300 °C |
10.1 µin/in-°F @Temperature 68.0 - 572 °F |
|
Eagle Brass 521 Phosphor Bronzes 8% C, Extra Spring Alloy C521 is a high tin alloy of the phosphor bronze family. The additional tin relative to the more commonly used C510 results in higher mechanical properties with a modest reduction in electrical.. |
|||
CTE, linear | 18.2 µm/m-°C @Temperature 20.0 - 300 °C |
10.1 µin/in-°F @Temperature 68.0 - 572 °F |
|
Eagle Brass 521 Phosphor Bronzes 8% C, Hard Alloy C521 is a high tin alloy of the phosphor bronze family. The additional tin relative to the more commonly used C510 results in higher mechanical properties with a modest reduction in electrical.. |
|||
CTE, linear | 18.2 µm/m-°C @Temperature 20.0 - 300 °C |
10.1 µin/in-°F @Temperature 68.0 - 572 °F |
|
Eagle Brass 521 Phosphor Bronzes 8% C, Spring Alloy C521 is a high tin alloy of the phosphor bronze family. The additional tin relative to the more commonly used C510 results in higher mechanical properties with a modest reduction in electrical.. |