Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 612 Â°F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	322 Â°C	612 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP LUBRICOMP LFL36E PEEK LNP* LUBRICOMP* LFL36E is a compound based on Polyetheretherketone containing 30% Glass Fiber, 15% PTFE. Added features of this material are: Wear Resistant, Easy Molding.
Deflection Temperature at 1.8 MPa (264 psi)	322 Â°C @Thickness 3.20 mm	612 Â°F @Thickness 0.126 in	unannealed; ASTM D648
SABIC Innovative Plastics LNP LUBRICOMP LX91475 PEEK LNP* LUBRICOMP* LX91475 is a compound based on Polyetheretherketone resin containing proprietary fillers. Added features of this material include: Easy Molding, High Temperature Bearing Grade, Wear..
Deflection Temperature at 1.8 MPa (264 psi)	322 Â°C @Thickness 3.20 mm	612 Â°F @Thickness 0.126 in	unannealed; ASTM D648
SABIC Innovative Plastics LNP THERMOCOMP LC008E PEEK LNP* THERMOCOMP* LC008E is a compound based on Polyetheretherketone resin containing 40% Carbon Fiber. Added features of this material include: Easy Molding, Electrically Conductive.
Deflection Temperature at 1.8 MPa (264 psi)	322 Â°C @Thickness 3.20 mm	612 Â°F @Thickness 0.126 in	unannealed; ASTM D648
SABIC Innovative Plastics LNP THERMOCOMP LC008E PEEK (Asia Pacific) LNP* Thermocomp* LC008E is a compound based on Polyetheretherketone resin containing Carbon Fiber. Added features of this material include: Easy Molding, Electrically Conductive.