SABIC Innovative Plastics LNP LUBRICOMP LX91475 PEEK

Category Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP LX91475 PEEK.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* LUBRICOMP* LX91475 is a compound based on Polyetheretherketone resin containing proprietary fillers. Added features of this material include: Easy Molding, High Temperature Bearing Grade, Wear Resistant.
Physical Properties Metric English Comments
Specific Gravity 1.40 g/cc
1.40 g/cc
ASTM D792
Density 1.43 g/cc
0.0517 lb/in³
ASTM D792
Moisture Absorption 0.0500 %
0.0500 %
50% RH, 24 hrs; ASTM D570
0.0800 %
0.0800 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm

@Time 86400 sec
0.0040 - 0.0060 in/in

@Time 24.0 hour
ASTM D955
Linear Mold Shrinkage, Transverse 0.0070 - 0.0090 cm/cm

@Time 86400 sec
0.0070 - 0.0090 in/in

@Time 24.0 hour
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 159 MPa
23100 psi
Type I, 5 mm/min; ASTM D638
160 MPa
23200 psi
5 mm/min; ISO 527
Tensile Strength, Yield 161 MPa
23400 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 2.1 %
2.1 %
Type I, 5 mm/min; ASTM D638
2.1 %
2.1 %
5 mm/min; ISO 527
Tensile Modulus 11.87 GPa
1722 ksi
1 mm/min; ISO 527
12.36 GPa
1793 ksi
5 mm/min; ASTM D638
Flexural Strength 229 MPa
33200 psi
ISO 178
239 MPa
34700 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 10.3 GPa
1490 ksi
1.3 mm/min, 50 mm span; ASTM D790
10.32 GPa
1497 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.580 J/cm
1.09 ft-lb/in
ASTM D256
Izod Impact, Unnotched 4.83 J/cm
9.05 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 30.0 kJ/m²
14.3 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 7.00 J

@Temperature 23.0 °C
5.16 ft-lb

@Temperature 73.4 °F
ASTM D3763
Impact Test 2.00 J
1.48 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.34
0.34
ASTM D3702 Modified
Coefficient of Friction, Static 0.42
0.42
ASTM D3702 Modified
K (wear) Factor 4.03 x 10-8 mm³/N-M
2.00 x 10-10 in³-min/ft-lb-hr
Ring; ASTM D3702 Modified
32.2 x 10-8 mm³/N-M
16.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 18.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
10.0 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D696
CTE, linear, Transverse to Flow 42.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
23.3 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 335 °C
635 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
336 °C

@Thickness 3.20 mm
637 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 335 °C
635 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
322 °C

@Thickness 3.20 mm
612 °F

@Thickness 0.126 in
unannealed; ASTM D648