Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 8.0 MPa | 45.0 - 50.0 °C | 113 - 122 °F | Average value: 46.4 °C Grade Count:10 |
Overview of materials for Polybutylene Terephthalate (PBT), Extrusion Grade This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Extrusion Grade". Each property range of values reported is minimum an.. |
|||
Deflection Temperature at 8.0 MPa | 45.0 °C | 113 °F | ISO 75-1/-2 |
Lanxess Durethan® B 30 S 000000 Nylon 6 PA 6, injection molding-grade, non-reinforced, easy-flow, easy-release, rapid solidification |
|||
Deflection Temperature at 8.0 MPa | 45.0 °C | 113 °F | ISO 75-1,-2 |
Lanxess Durethan® B 40 SK 000000 Nylon 6 PA 6, non-reinforced, injection molding |
|||
Deflection Temperature at 8.0 MPa | 45.0 °C | 113 °F | ISO 75-1/-2 |
Lanxess Durethan® BC 30 000000 Nylon 6 PA 6, injection molding grade, non-reinforced, rapid processing, higher notched impact strength than B 30 S / B 31 SK in dry and conditioned state, impact-modified |
|||
Deflection Temperature at 8.0 MPa | 45.0 °C | 113 °F | ISO 75-1/-2 |
Lanxess Durethan® BC 40 SR2 000000 Nylon 6 PA 6 injection molding grade, high viscosity, non-reinforced, higher notched impact strength than BC 30, impact-modified |
|||
Deflection Temperature at 8.0 MPa | 45.0 °C | 113 °F | ISO 75-1/-2 |
Lanxess Pocan® B 1300 000000 PBT PBT, non-reinforced, injection molding, extrusion |
|||
Deflection Temperature at 8.0 MPa | 45.0 °C | 113 °F | ISO 75-1/-2 |
Lanxess Pocan® B 1305 000000 PBT PBT, non-reinforced, injection molding |
|||
Deflection Temperature at 8.0 MPa | 45.0 °C | 113 °F | ISO 75-1/-2 |
Lanxess Pocan® B 1501 000000 PBT PBT, non-reinforced, injection molding, extrusion, food contact |
|||
Deflection Temperature at 8.0 MPa | 45.0 °C | 113 °F | ISO 75-1/-2 |
Lanxess Pocan® B 1700 000000 PBT PBT, non-reinforced, extrusion, food contact |
|||
Deflection Temperature at 8.0 MPa | 45.0 °C | 113 °F | ISO 75-1/-2 |
Lanxess Pocan® B 1505 000000 PBT PBT, non-reinforced, injection molding, extrusion |
|||
Deflection Temperature at 8.0 MPa | 45.0 °C | 113 °F | ISO 75-1/-2 |
EMS-Grivory Grivory® BK-50 PA6-GB50 Information provided by EMS Grivory |
|||
Deflection Temperature at 8.0 MPa | 45.0 °C | 113 °F | ISO 75-1/-2 |
Lanxess Pocan® B 1600 000000 PBT PBT, non-reinforced, injection molding, extrusion, food contact |