Polymer Property : Deflection Temperature at 8.0 MPa = 113 °F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Deflection Temperature at 8.0 MPa 45.0 - 50.0 °C
113 - 122 °F
Average value: 46.4 °C Grade Count:10
Overview of materials for Polybutylene Terephthalate (PBT), Extrusion Grade
This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Extrusion Grade". Each property range of values reported is minimum an..
Deflection Temperature at 8.0 MPa 45.0 °C
113 °F
ISO 75-1/-2
Lanxess Durethan® B 30 S 000000 Nylon 6
PA 6, injection molding-grade, non-reinforced, easy-flow, easy-release, rapid solidification
Deflection Temperature at 8.0 MPa 45.0 °C
113 °F
ISO 75-1,-2
Lanxess Durethan® B 40 SK 000000 Nylon 6
PA 6, non-reinforced, injection molding
Deflection Temperature at 8.0 MPa 45.0 °C
113 °F
ISO 75-1/-2
Lanxess Durethan® BC 30 000000 Nylon 6
PA 6, injection molding grade, non-reinforced, rapid processing, higher notched impact strength than B 30 S / B 31 SK in dry and conditioned state, impact-modified
Deflection Temperature at 8.0 MPa 45.0 °C
113 °F
ISO 75-1/-2
Lanxess Durethan® BC 40 SR2 000000 Nylon 6
PA 6 injection molding grade, high viscosity, non-reinforced, higher notched impact strength than BC 30, impact-modified
Deflection Temperature at 8.0 MPa 45.0 °C
113 °F
ISO 75-1/-2
Lanxess Pocan® B 1300 000000 PBT
PBT, non-reinforced, injection molding, extrusion
Deflection Temperature at 8.0 MPa 45.0 °C
113 °F
ISO 75-1/-2
Lanxess Pocan® B 1305 000000 PBT
PBT, non-reinforced, injection molding
Deflection Temperature at 8.0 MPa 45.0 °C
113 °F
ISO 75-1/-2
Lanxess Pocan® B 1501 000000 PBT
PBT, non-reinforced, injection molding, extrusion, food contact
Deflection Temperature at 8.0 MPa 45.0 °C
113 °F
ISO 75-1/-2
Lanxess Pocan® B 1700 000000 PBT
PBT, non-reinforced, extrusion, food contact
Deflection Temperature at 8.0 MPa 45.0 °C
113 °F
ISO 75-1/-2
Lanxess Pocan® B 1505 000000 PBT
PBT, non-reinforced, injection molding, extrusion
Deflection Temperature at 8.0 MPa 45.0 °C
113 °F
ISO 75-1/-2
EMS-Grivory Grivory® BK-50 PA6-GB50
Information provided by EMS Grivory
Deflection Temperature at 8.0 MPa 45.0 °C
113 °F
ISO 75-1/-2
Lanxess Pocan® B 1600 000000 PBT
PBT, non-reinforced, injection molding, extrusion, food contact