Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 369 °F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	187 °C	369 °F	DIN 53461
Qualchem Danamid AFES-21 Polyamide 66 Impact resistant, dryInformation provided by Qualchem Zrt.
Deflection Temperature at 0.46 MPa (66 psi)	187 Â°C @Thickness 3.20 mm	369 Â°F @Thickness 0.126 in	unannealed; ASTM D648
SABIC Innovative Plastics LNP LUBRICOMP IAL12 PA6.12 LNP* LUBRICOMP* IAL12 is a compound based on Nylon 6/12 resin containing 5% PTFE, 10% Aramid Fiber. Added features of this material include: Internally Lubricated.
Deflection Temperature at 0.46 MPa (66 psi)	187 Â°C @Thickness 6.40 mm	369 Â°F @Thickness 0.252 in	unannealed; ASTM D648
SABIC Innovative Plastics ValoxÂ® EH7020 PBT MINERAL FILLED, METALLIZABLE
Deflection Temperature at 0.46 MPa (66 psi)	187 Â°C @Thickness 6.40 mm	369 Â°F @Thickness 0.252 in	unannealed; ASTM D648
SABIC Innovative Plastics ValoxÂ® EH7020 PBT (Asia Pacific)
Deflection Temperature at 0.46 MPa (66 psi)	187 Â°C @Thickness 3.20 mm	369 Â°F @Thickness 0.126 in	unannealed; ASTM D 648
SABIC Innovative Plastics LNP Thermocomp YF006 TPEE LNP THERMOCOMP* YF006 is a compound based on TPEE resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region.
Deflection Temperature at 0.46 MPa (66 psi)	187 Â°C	369 Â°F	Flatw 80104 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics NORYL GTX GTX9400W PPE+PS+PA High flow PPO+PA. Power distribution box applications.
Deflection Temperature at 0.46 MPa (66 psi)	187 Â°C	369 Â°F	Flatw 80104 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics NORYL GTX GTX9400W PPE+PS+PA (Asia Pacific) High flow PPO+PA. Power distribution box applications.
Deflection Temperature at 0.46 MPa (66 psi)	187 Â°C @Thickness 3.20 mm	369 Â°F @Thickness 0.126 in	unannealed; ASTM D648
SABIC Innovative Plastics NORYL GTX GTX673 PPE+PA Conductive Noryl GTX* resin designed for profile extrusion. This grade can be electrostatic or powder coat painted without the need for a primer. In addition, its high heat capability allows it to ..
Deflection Temperature at 0.46 MPa (66 psi)	187 Â°C	369 Â°F	Flatw 80104 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics NORYL GTX GTX675 PPE+PA6 Noryl GTX* GTX675 Resin is a blend of Polyphenylene Ether(PPE) + Polyamide(PA) resin that is mineral filled, conductive, and suitable for injection molding. The conductivity level is optimized to a..
Deflection Temperature at 0.46 MPa (66 psi)	187 Â°C @Thickness 3.20 mm	369 Â°F @Thickness 0.126 in	unannealed; ASTM D648
SABIC Innovative Plastics NORYL GTX GTX675 PPE+PA6 Noryl GTX* GTX675 Resin is a blend of Polyphenylene Ether(PPE) + Polyamide(PA) resin that is mineral filled, conductive, and suitable for injection molding. The conductivity level is optimized to a..
Deflection Temperature at 0.46 MPa (66 psi)	187 °C	369 °F	ASTM D648
A. Schulman ComAlloy Comtuf® 602 Nylon 6/6, High Impact Modified Data provided by the manufacturer, ComAlloy International Company. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been integrated into the A Sc..
Deflection Temperature at 0.46 MPa (66 psi)	187 °C	369 °F	Flatw 80104 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics LNP Thermocomp TX88477 PU LNP* Thermocomp* TX88447 is a compound based on Polyurethane resin containing proprietary fillers.This data was supplied by SABIC-IP for the Americas region.
Deflection Temperature at 0.46 MPa (66 psi)	187 - 190 °C	369 - 374 °F	Average value: 188 °C Grade Count:3
Overview of materials for Polysulfone, 30% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polysulfone, 30% Glass Fiber Reinforced". Specific grades with glass content between 25% and 34% are inc..