Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 17.9 - 18.9 µm/m-°C @Temperature 20.0 - 100 °C |
9.94 - 10.5 µin/in-°F @Temperature 68.0 - 212 °F |
|
PEAK Werkstoff DISPAL S232 Aluminum Alloy, AlSi17Fe4Cu3Mg, Condition T6 Heat Treatment Condition T6 (Quench in water at RT). Excellent properties:abrasive stabilityhigh stiffness (E-modulus)resistance even at high temperaturesgood grindabilityPEAK DISPAL materials allo.. |
|||
CTE, linear | 17.9 - 18.9 µm/m-°C @Temperature 20.0 - 100 °C |
9.94 - 10.5 µin/in-°F @Temperature 68.0 - 212 °F |
|
PEAK Werkstoff DISPAL S232 Aluminum Alloy, AlSi17Fe4Cu3Mg, Condition T6x Heat Treatment Condition T6x (Quench in water at RT). Excellent properties:abrasive stabilityhigh stiffness (E-modulus)resistance even at high temperaturesgood grindabilityPEAK DISPAL materials all.. |
|||
CTE, linear | 17.9 µm/m-°C @Temperature 25.0 - 1000 °C |
9.94 µin/in-°F @Temperature 77.0 - 1830 °F |
|
Haynes 188 alloy, 0% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 17.9 µm/m-°C @Temperature 25.0 - 1000 °C |
9.94 µin/in-°F @Temperature 77.0 - 1830 °F |
|
Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 17.9 µm/m-°C @Temperature 25.0 - 1000 °C |
9.94 µin/in-°F @Temperature 77.0 - 1830 °F |
|
Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 17.9 µm/m-°C @Temperature 25.0 - 1000 °C |
9.94 µin/in-°F @Temperature 77.0 - 1830 °F |
|
Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 17.9 µm/m-°C @Temperature 25.0 - 1000 °C |
9.94 µin/in-°F @Temperature 77.0 - 1830 °F |
|
Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 17.9 µm/m-°C @Temperature 25.0 - 1000 °C |
9.94 µin/in-°F @Temperature 77.0 - 1830 °F |
|
Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 17.9 µm/m-°C @Temperature 25.0 - 1000 °C |
9.94 µin/in-°F @Temperature 77.0 - 1830 °F |
|
Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 17.9 µm/m-°C @Temperature 25.0 - 1000 °C |
9.94 µin/in-°F @Temperature 77.0 - 1830 °F |
|
Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 17.9 µm/m-°C @Temperature 25.0 - 1000 °C |
9.94 µin/in-°F @Temperature 77.0 - 1830 °F |
|
Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 17.9 µm/m-°C @Temperature 25.0 - 1000 °C |
9.94 µin/in-°F @Temperature 77.0 - 1830 °F |
|
Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 17.9 µm/m-°C @Temperature 25.0 - 1000 °C |
9.94 µin/in-°F @Temperature 77.0 - 1830 °F |
|
Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 17.9 µm/m-°C @Temperature 25.0 - 1000 °C |
9.94 µin/in-°F @Temperature 77.0 - 1830 °F |
|
Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 17.9 µm/m-°C @Temperature 25.0 - 1000 °C |
9.94 µin/in-°F @Temperature 77.0 - 1830 °F |
|
Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 17.9 µm/m-°C @Temperature 25.0 - 1000 °C |
9.94 µin/in-°F @Temperature 77.0 - 1830 °F |
|
Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 17.9 µm/m-°C @Temperature 25.0 - 1000 °C |
9.94 µin/in-°F @Temperature 77.0 - 1830 °F |
|
Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 17.9 µm/m-°C @Temperature 25.0 - 1000 °C |
9.94 µin/in-°F @Temperature 77.0 - 1830 °F |
|
Haynes 188 alloy, hot rolled and 1175°C solution annealed plate Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 17.9 µm/m-°C @Temperature 25.0 - 1000 °C |
9.94 µin/in-°F @Temperature 77.0 - 1830 °F |
|
Haynes 188 alloy, plate at RT after 0 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 17.9 µm/m-°C @Temperature 25.0 - 1000 °C |
9.94 µin/in-°F @Temperature 77.0 - 1830 °F |
|
Haynes 188 alloy, plate at RT after 1000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 17.9 µm/m-°C @Temperature 25.0 - 1000 °C |
9.94 µin/in-°F @Temperature 77.0 - 1830 °F |
|
Haynes 188 alloy, plate at RT after 16000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 17.9 µm/m-°C @Temperature 25.0 - 1000 °C |
9.94 µin/in-°F @Temperature 77.0 - 1830 °F |
|
Haynes 188 alloy, plate at RT after 4000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 17.9 µm/m-°C @Temperature 25.0 - 1000 °C |
9.94 µin/in-°F @Temperature 77.0 - 1830 °F |
|
Haynes 188 alloy, plate at RT after 8000 hours at 650°C (1200°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 17.9 µm/m-°C @Temperature 25.0 - 1000 °C |
9.94 µin/in-°F @Temperature 77.0 - 1830 °F |
|
Haynes 188 alloy, plate at RT after 8000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 17.9 µm/m-°C @Temperature 20.0 - 1000 °C |
9.94 µin/in-°F @Temperature 68.0 - 1830 °F |
|
Haynes X-750 Nickel Alloy Sheet and Strip (AMS 5598, UNS N07750) Haynes X-750 (UNS No. N07750) alloy is an age-hardenable, nickel-base superalloy with very good strength at temperatures up to about 1600°F (870°C). It is widely used as a wrought material for.. |
|||
CTE, linear | 17.9 µm/m-°C @Temperature 25.0 - 1000 °C |
9.94 µin/in-°F @Temperature 77.0 - 1830 °F |
|
Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 17.9 µm/m-°C @Temperature 25.0 - 1000 °C |
9.94 µin/in-°F @Temperature 77.0 - 1830 °F |
|
Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 17.9 µm/m-°C @Temperature 25.0 - 1000 °C |
9.94 µin/in-°F @Temperature 77.0 - 1830 °F |
|
Haynes 188 alloy, cold rolled and 1175°C solution annealed sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 17.9 µm/m-°C @Temperature 25.0 - 1000 °C |
9.94 µin/in-°F @Temperature 77.0 - 1830 °F |
|
Haynes 188 alloy, plate at RT after 8000 hours at 760°C (1400°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |