- PEAK Werkstoff DISPAL S232 Aluminum Alloy, AlSi17Fe4Cu3Mg, Condition T6
PEAK Werkstoff DISPAL S232 Aluminum Alloy, AlSi17Fe4Cu3Mg, Condition T6
| Category | Metal , Nonferrous Metal , Aluminum Alloy |
| Manufacturer | PEAK Werkstoff |
| Trade Name | DISPAL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PEAK Werkstoff DISPAL S232 Aluminum Alloy, AlSi17Fe4Cu3Mg, Condition T6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Heat Treatment Condition T6 (Quench in water at RT). Excellent properties:abrasive stabilityhigh stiffness (E-modulus)resistance even at high temperaturesgood grindabilityPEAK DISPAL materials allow the manufacturing of pistons for highest operational demands.Information provided by PEAK Werkstoff GmbH
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.651 - 2.930 g/cc | 0.09576 - 0.1058 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Vickers | >= 175 | >= 175 | HV30 |
| Tensile Strength at Break | >= 490 MPa | >= 71100 psi | |
| Tensile Strength, Yield | >= 448 MPa | >= 65000 psi | |
| Elongation at Break | >= 0.60 % | >= 0.60 % | |
| Modulus of Elasticity | >= 88.0 GPa | >= 12800 ksi | |
| >= 76.0 GPa @Temperature 200 °C |
>= 11000 ksi @Temperature 392 °F |
Condition T6x (Quench in water at RT) | |
| >= 80.0 GPa @Temperature 150 °C |
>= 11600 ksi @Temperature 302 °F |
Condition T6x (Quench in water at RT) | |
| >= 88.0 GPa @Temperature 20.0 °C |
>= 12800 ksi @Temperature 68.0 °F |
Condition T6x (Quench in water at RT) | |
| Poissons Ratio | 0.332 @Temperature 20.0 °C |
0.332 @Temperature 68.0 °F |
Condition T6x (Quench in water at RT) |
| 0.334 @Temperature 100 °C |
0.334 @Temperature 212 °F |
Condition T6x (Quench in water at RT) | |
| 0.337 @Temperature 150 °C |
0.337 @Temperature 302 °F |
Condition T6x (Quench in water at RT) | |
| 0.339 @Temperature 200 °C |
0.339 @Temperature 392 °F |
Condition T6x (Quench in water at RT) | |
| 0.342 @Temperature 250 °C |
0.342 @Temperature 482 °F |
Condition T6x (Quench in water at RT) | |
| 0.343 @Temperature 300 °C |
0.343 @Temperature 572 °F |
Condition T6x (Quench in water at RT) | |
| Fatigue Strength | 225.4 MPa | 32690 psi | Condition T6x (Quench in water at RT) |
| Shear Modulus | 31.0 GPa @Temperature 300 °C |
4500 ksi @Temperature 572 °F |
Condition T6x (Quench in water at RT) |
| 31.0 GPa @Temperature 250 °C |
4500 ksi @Temperature 482 °F |
Condition T6x (Quench in water at RT) | |
| 32.0 GPa @Temperature 200 °C |
4640 ksi @Temperature 392 °F |
Condition T6x (Quench in water at RT) | |
| 33.0 GPa @Temperature 150 °C |
4790 ksi @Temperature 302 °F |
Condition T6x (Quench in water at RT) | |
| 34.0 GPa @Temperature 100 °C |
4930 ksi @Temperature 212 °F |
Condition T6x (Quench in water at RT) | |
| 35.0 GPa @Temperature 20.0 °C |
5080 ksi @Temperature 68.0 °F |
Condition T6x (Quench in water at RT) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 17.9 - 18.9 µm/m-°C @Temperature 20.0 - 100 °C |
9.94 - 10.5 µin/in-°F @Temperature 68.0 - 212 °F |
|
| 18.5 - 19.5 µm/m-°C @Temperature 20.0 - 200 °C |
10.3 - 10.8 µin/in-°F @Temperature 68.0 - 392 °F |
||
| 19.3 - 20.3 µm/m-°C @Temperature 20.0 - 300 °C |
10.7 - 11.3 µin/in-°F @Temperature 68.0 - 572 °F |
||
| Specific Heat Capacity | 0.860 - 0.900 J/g-°C | 0.206 - 0.215 BTU/lb-°F | |
| Thermal Conductivity | 116.8 W/m-K @Temperature 30.0 °C |
810.6 BTU-in/hr-ft²-°F @Temperature 86.0 °F |
|
| 117.9 W/m-K @Temperature 100 °C |
818.2 BTU-in/hr-ft²-°F @Temperature 212 °F |
||
| 122.1 W/m-K @Temperature 200 °C |
847.4 BTU-in/hr-ft²-°F @Temperature 392 °F |
||
| 125.7 W/m-K @Temperature 400 °C |
872.4 BTU-in/hr-ft²-°F @Temperature 752 °F |
||
| 131.7 W/m-K @Temperature 300 °C |
914.0 BTU-in/hr-ft²-°F @Temperature 572 °F |
||
| Melting Point | 516 - 738 °C | 961 - 1360 °F | |
| Solidus | 515.9 - 521.9 °C | 960.6 - 971.4 °F | |
| Liquidus | 731.5 - 737.5 °C | 1349 - 1360 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Aluminum, Al | 75 % | 75 % | As Balance |
| Copper, Cu | 3.0 % | 3.0 % | |
| Iron, Fe | 4.0 % | 4.0 % | |
| Magnesium, Mg | 1.0 % | 1.0 % | |
| Silicon, Si | 17 % | 17 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.00000750 - 0.00000810 ohm-cm | 0.00000750 - 0.00000810 ohm-cm |