Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 13.2 µm/m-°C @Temperature 0.000 - 700 °C |
7.33 µin/in-°F @Temperature 32.0 - 1290 °F |
|
Kennametal Stellite Stellite® STAR with P/M Processing Applications: Vane plugs, fuel metering pins, spacer bushings, ball bearing blanks, race bearing blanks, diesel engine exhaust, fluid valve seats, saw cutter inserts, wear pads, pins, balls, hardfa.. |
|||
CTE, linear | 13.2 µm/m-°C @Temperature 900 °C |
7.33 µin/in-°F @Temperature 1650 °F |
|
MarkeTech Repton EXP 22 Magnesia MgO REPTON setter tiles, kiln furniture, and special fixtures are lightweight, ridge, and high strength ceramics that resist distortion and spalling, even when thermal cycled many times. They are availa.. |
|||
CTE, linear | 13.2 µm/m-°C @Temperature 25.0 - 300 °C |
7.33 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 188 alloy, 0% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 13.2 µm/m-°C @Temperature 25.0 - 300 °C |
7.33 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 13.2 µm/m-°C @Temperature 25.0 - 300 °C |
7.33 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 13.2 µm/m-°C @Temperature 25.0 - 300 °C |
7.33 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 13.2 µm/m-°C @Temperature 25.0 - 300 °C |
7.33 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 13.2 µm/m-°C @Temperature 25.0 - 300 °C |
7.33 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 13.2 µm/m-°C @Temperature 25.0 - 300 °C |
7.33 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 13.2 µm/m-°C @Temperature 25.0 - 300 °C |
7.33 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 188 alloy, hot rolled and 1175°C solution annealed plate Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 13.2 µm/m-°C @Temperature 25.0 - 300 °C |
7.33 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 188 alloy, plate at RT after 0 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 13.2 µm/m-°C @Temperature 25.0 - 300 °C |
7.33 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 188 alloy, plate at RT after 16000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 13.2 µm/m-°C @Temperature 25.0 - 300 °C |
7.33 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 188 alloy, plate at RT after 8000 hours at 650°C (1200°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 13.2 µm/m-°C @Temperature 21.0 - 300 °C |
7.33 µin/in-°F @Temperature 69.8 - 572 °F |
|
Haynes Hastelloy® G-35® Nickel Alloy Plate, Annealed at 2025°F (1107°C) Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process†phosphoric acid, which is widely used in the production of fertilizers. Tests indicat.. |
|||
CTE, linear | 13.2 µm/m-°C @Temperature 20.0 - 600 °C |
7.33 µin/in-°F @Temperature 68.0 - 1110 °F |
|
Haynes Hastelloy® W alloy as a weld filler, base metal Alloy 625/ Alloy 718 12.7 mm plate weldments Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
CTE, linear | 13.2 µm/m-°C @Temperature 20.0 - 600 °C |
7.33 µin/in-°F @Temperature 68.0 - 1110 °F |
|
Haynes Hastelloy® W alloy as a weld filler, base metal Carbon steel 12.7 mm plate weldments Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
CTE, linear | 13.2 µm/m-°C @Temperature 20.0 - 600 °C |
7.33 µin/in-°F @Temperature 68.0 - 1110 °F |
|
Haynes Hastelloy® W alloy as a weld filler, base metal Type 304 Carbon steel 12.7 mm plate weldments Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
CTE, linear | 13.2 µm/m-°C @Temperature 20.0 - 600 °C |
7.33 µin/in-°F @Temperature 68.0 - 1110 °F |
|
Haynes Hastelloy® W alloy as a weld filler, base metal Type 304 Stainless steel 12.7 mm plate weldments Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
CTE, linear | 13.2 µm/m-°C @Temperature 20.0 - 600 °C |
7.33 µin/in-°F @Temperature 68.0 - 1110 °F |
|
Haynes Hastelloy® W alloy, gas metal arc welds, as-welded Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
CTE, linear | 13.2 µm/m-°C @Temperature 20.0 - 600 °C |
7.33 µin/in-°F @Temperature 68.0 - 1110 °F |
|
Haynes Hastelloy® W alloy, gas tungsten arc welds, aged 1000 hours at 650°C (1200°F) Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
CTE, linear | 13.2 µm/m-°C @Temperature 20.0 - 600 °C |
7.33 µin/in-°F @Temperature 68.0 - 1110 °F |
|
Haynes Hastelloy® W alloy, shielded metal arc welds, as-welded Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
CTE, linear | 13.2 µm/m-°C @Temperature 25.0 - 300 °C |
7.33 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 188 alloy, cold rolled and 1175°C solution annealed sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 13.2 µm/m-°C @Temperature 25.0 - 300 °C |
7.33 µin/in-°F @Temperature 77.0 - 572 °F |
|
Haynes 188 alloy, plate at RT after 8000 hours at 760°C (1400°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 13.2 µm/m-°C @Temperature 20.0 - 500 °C |
7.33 µin/in-°F @Temperature 68.0 - 932 °F |
|
Haynes Hastelloy® alloy 718 12.7 mm plate weldments Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
CTE, linear | 13.2 µm/m-°C @Temperature 20.0 - 500 °C |
7.33 µin/in-°F @Temperature 68.0 - 932 °F |
|
Haynes Hastelloy® alloy X 12.7 mm plate weldments Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
CTE, linear | 13.2 µm/m-°C @Temperature 400 °C |
7.33 µin/in-°F @Temperature 752 °F |
|
Bohler-Uddeholm BÖHLER M261 Extra Plastic Lens Mold Steel VACUUM ARC REMELTED HARDENED AND TEMPERED PLASTIC LENS MOLD STEELBOHLER M261 follow current trends in tool and die-making:Excellent machinability coupled with higher hardnessGood dimensional stabili.. |
|||
CTE, linear | 13.2 µm/m-°C @Temperature 20.0 - 700 °C |
7.33 µin/in-°F @Temperature 68.0 - 1290 °F |
|
Bohler-Uddeholm BÖHLER W302 SUPERIOR® Premium H13 Tool Steel A premium grade H13 hot work tool steel featuring:Very good toughness properties meeting the requirements of NADCA 207-97, and the superior quality levels of NADCA 207-2003Very good heat checking re.. |
|||
CTE, linear | 13.2 µm/m-°C @Temperature 20.0 - 700 °C |
7.33 µin/in-°F @Temperature 68.0 - 1290 °F |
|
Bohler-Uddeholm BÖHLER W400 VMR® H11 Hot Work Tool Steel W400 VMR is a low silicon, chromium-vanadium hot work tool steel which has been vacuum remelted to obtain the highest uniformity, the best cleanliness of tool steel. The material is characterized:E.. |
|||
CTE, linear | 13.2 µm/m-°C @Temperature 20.0 - 700 °C |
7.33 µin/in-°F @Temperature 68.0 - 1290 °F |
|
Bohler-Uddeholm BÖHLER W403 VMR® Hot Work Tool Steel W403 VMR is a modified hot work alloy with an excellent combination of hot tensile properties and toughness. The balanced properties of this grade are not only due to chemistry modification, but to .. |
|||
CTE, linear | 13.2 µm/m-°C @Temperature 20.0 - 600 °C |
7.33 µin/in-°F @Temperature 68.0 - 1110 °F |
|
Bohler-Uddeholm BÖHLER W360 ISOBLOC® Hot Work Tool Steel BÖHLER W360 ISOBLOC was developed as a tool steel for dies and punches in warm and hot forging. The steel can be used for a variety of applications where hardness and toughness are required. Prope.. |