Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear, Transverse to Flow | 42.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
23.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
SABIC Innovative Plastics LNP LUBRICOMP LCL36E PEEK (Europe-Africa-Middle East) LNP* LUBRICOMP* LCL36E is a compound based on Polyetheretherketone resin containing Carbon Fiber , PTFE. Added features include : Electrically Conductive, Internally Lubricated, Easy Molding. |
|||
CTE, linear, Transverse to Flow | 42.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
23.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
SABIC Innovative Plastics LNP LUBRICOMP LX91475 PEEK LNP* LUBRICOMP* LX91475 is a compound based on Polyetheretherketone resin containing proprietary fillers. Added features of this material include: Easy Molding, High Temperature Bearing Grade, Wear.. |
|||
CTE, linear, Transverse to Flow | 42.0 µm/m-°C @Temperature 23.0 - 150 °C |
23.3 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 |
SABIC Innovative Plastics ULTEM AR9300 PEI (Europe-Africa-Middle East) 30% Glass fiber filled, standard flow Polyetherimide (Tg 217C). Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke, and flame evolution. |
|||
CTE, linear, Transverse to Flow | 42.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
23.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
SABIC Innovative Plastics LNP THERMOCOMP DF00A1P PC (Asia Pacific) LNP* Thermocomp* DF00AIP is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: High Modulus, low warpage, Non-Brominated & Non.. |
|||
CTE, linear, Transverse to Flow | 42.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
23.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
SABIC Innovative Plastics LNP THERMOCOMP LC006 PEEK (Europe-Africa-Middle East) LNP* THERMOCOMP* LC006 is a compound based on Polyetheretherketone containing Carbon Fiber. Added features include: Electrically Conductive. |
|||
CTE, linear, Transverse to Flow | 42.0 µm/m-°C @Temperature 20.0 °C |
23.3 µin/in-°F @Temperature 68.0 °F |
|
Covestro Baygal® 90 IK 69 Polyurethane Uses: Suitable for impregnation and encapsulation of coils, especially when high heat deflection temperature, and eventually fire resistance is requested.Information provided by Bayer.As of 1 Septem.. |
|||
CTE, linear, Transverse to Flow | 42.0 µm/m-°C @Temperature 20.0 °C |
23.3 µin/in-°F @Temperature 68.0 °F |
ASTM E-831 |
Sumitomo Bakelite North America RX® 852 Novolac Phenolic Fiberglass reinforced phenolic novolac compound with good dimensional stability and good strength at elevated temperatures.Information provided by Vyncolit, a Sumitomo Bak Group |