Polymer Property : Specific Heat Capacity = 0.431 J/g-°C Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Specific Heat Capacity 0.431 J/g-°C

@Temperature 300 °C
 0.103 BTU/lb-°F

@Temperature 572 °F
Haynes 242® alloy, cold reduced sheet, annealed, 20% cold work
Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm..
Specific Heat Capacity 0.431 J/g-°C

@Temperature 300 °C
 0.103 BTU/lb-°F

@Temperature 572 °F
Haynes 242® alloy
Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm..
Specific Heat Capacity 0.431 J/g-°C

@Temperature 300 °C
 0.103 BTU/lb-°F

@Temperature 572 °F
Haynes 242® alloy, after 1000 hours exposure at 650°C (1200°F)
Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm..
Specific Heat Capacity 0.431 J/g-°C

@Temperature 300 °C
 0.103 BTU/lb-°F

@Temperature 572 °F
Haynes 242® alloy, after 4000 hours exposure at 650°C (1200°F)
Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm..
Specific Heat Capacity 0.431 J/g-°C

@Temperature 300 °C
 0.103 BTU/lb-°F

@Temperature 572 °F
Haynes 242® alloy, after 8000 hours exposure at 650°C (1200°F)
Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm..
Specific Heat Capacity 0.431 J/g-°C

@Temperature 300 °C
 0.103 BTU/lb-°F

@Temperature 572 °F
Haynes 242® alloy, cold reduced sheet, annealed
Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm..
Specific Heat Capacity 0.431 J/g-°C

@Temperature 300 °C
 0.103 BTU/lb-°F

@Temperature 572 °F
Haynes 242® alloy, cold reduced sheet, annealed and 20% cold work
Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm..
Specific Heat Capacity 0.431 J/g-°C

@Temperature 300 °C
 0.103 BTU/lb-°F

@Temperature 572 °F
Haynes 242® alloy, cold reduced sheet, annealed and 40% cold work
Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm..
Specific Heat Capacity 0.431 J/g-°C

@Temperature 300 °C
 0.103 BTU/lb-°F

@Temperature 572 °F
Haynes 242® alloy, cold reduced sheet, annealed and aged
Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm..
Specific Heat Capacity 0.431 J/g-°C

@Temperature 300 °C
 0.103 BTU/lb-°F

@Temperature 572 °F
Haynes 242® alloy, cold reduced sheet, annealed, 40% cold work, aged
Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm..
Specific Heat Capacity 0.431 J/g-°C

@Temperature 400 °C
 0.103 BTU/lb-°F

@Temperature 752 °F
Haynes Hastelloy® B-3® alloy, 0% cold work
The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and ..
Specific Heat Capacity 0.431 J/g-°C

@Temperature 400 °C
 0.103 BTU/lb-°F

@Temperature 752 °F
Haynes Hastelloy® B-3® alloy, 10% cold work
The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and ..
Specific Heat Capacity 0.431 J/g-°C

@Temperature 400 °C
 0.103 BTU/lb-°F

@Temperature 752 °F
Haynes Hastelloy® B-3® alloy, 20% cold work
The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and ..
Specific Heat Capacity 0.431 J/g-°C

@Temperature 400 °C
 0.103 BTU/lb-°F

@Temperature 752 °F
Haynes Hastelloy® B-3® alloy, 3.2 mm bright annealed sheet
The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and ..
Specific Heat Capacity 0.431 J/g-°C

@Temperature 400 °C
 0.103 BTU/lb-°F

@Temperature 752 °F
Haynes Hastelloy® B-3® alloy, 30% cold work
The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and ..
Specific Heat Capacity 0.431 J/g-°C

@Temperature 400 °C
 0.103 BTU/lb-°F

@Temperature 752 °F
Haynes Hastelloy® B-3® alloy, 40% cold work
The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and ..
Specific Heat Capacity 0.431 J/g-°C

@Temperature 400 °C
 0.103 BTU/lb-°F

@Temperature 752 °F
Haynes Hastelloy® B-3® alloy, 50% cold work
The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and ..
Specific Heat Capacity 0.431 J/g-°C

@Temperature 400 °C
 0.103 BTU/lb-°F

@Temperature 752 °F
Haynes Hastelloy® B-3® alloy, 6.3 mm plate
The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and ..
Specific Heat Capacity 0.431 J/g-°C
0.103 BTU/lb-°F
Special Metals INCOLOY® Alloy 907
A nickel-iron-cobalt alloy with additions of niobium and titanium for precipitation hardening. It has the low coefficient of expansion and high strength of INCOLOY alloy 903 but with improved notch..
Specific Heat Capacity 0.431 J/g-°C
0.103 BTU/lb-°F
Special Metals INCONEL® Alloy 751
A nickel-chromium alloy similar to INCONEL ALLOY X-750 but with increased aluminum content for greater precipitation hardening. INCONEL alloy 751 was designed for use as exhaust valves in internal-..
Specific Heat Capacity 0.431 J/g-°C
0.103 BTU/lb-°F
Special Metals INCONEL® Alloy X-750
A nickel-chromium alloy similar to INCONEL alloy 600 but made precipitation hardenable by additions of aluminum and titanium. The alloy has good resistance to corrosion and oxidation along with hig..
Specific Heat Capacity 0.431 J/g-°C
0.103 BTU/lb-°F
Special Metals NIMONIC® Alloy 901
A nickel-iron-chromium alloy containing titanium and aluminum for precipitation hardening and molybdenum for solid-solution strengthening. The alloy has high yield strength and creep resistance at ..
Specific Heat Capacity 0.431 J/g-°C
0.103 BTU/lb-°F
Bohler-Uddeholm BÖHLER S500(m42) High Speed Steel
Description: Cobalt Molybdenum high speed steel processing high hardness, excellent cutting properties, high red hardness and good toughness. BOHLER S500 is also available in the special grade ISORA..
Specific Heat Capacity 0.431 J/g-°C

@Temperature 400 °C
 0.103 BTU/lb-°F

@Temperature 752 °F
Haynes Hastelloy® B-3® alloy, heat treated at 1065°C, rapid quenched
The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and ea..