- Polymer Property : Specific Heat Capacity = 0.141 BTU/lb-°F
Polymer Property : Specific Heat Capacity = 0.141 BTU/lb-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Heat Capacity | 0.590 J/g-°C @Temperature 300 °C |
0.141 BTU/lb-°F @Temperature 572 °F |
|
| Outokumpu SAF 2304® Duplex Stainless Steel Applications: Pulp and paper industryDesalination plantsFlue-gas cleaningCargo tanks and pipe systems in chemical tankersSeawater systemsFirewalls and blast walls on offshore platformsBridgesCompone.. |
|||
| Specific Heat Capacity | 0.590 J/g-°C @Temperature 300 °C |
0.141 BTU/lb-°F @Temperature 572 °F |
|
| Outokumpu SAF 2507® Duplex Stainless Steel Applications: Pulp and paper industryDesalination plantsFlue-gas cleaningCargo tanks and pipe systems in chemical tankersSeawater systemsFirewalls and blast walls on offshore platformsBridgesCompone.. |
|||
| Specific Heat Capacity | 0.590 J/g-°C @Temperature 1000 °C |
0.141 BTU/lb-°F @Temperature 1830 °F |
|
| Haynes 188 alloy, 0% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.590 J/g-°C @Temperature 1000 °C |
0.141 BTU/lb-°F @Temperature 1830 °F |
|
| Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.590 J/g-°C @Temperature 1000 °C |
0.141 BTU/lb-°F @Temperature 1830 °F |
|
| Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.590 J/g-°C @Temperature 1000 °C |
0.141 BTU/lb-°F @Temperature 1830 °F |
|
| Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.590 J/g-°C @Temperature 1000 °C |
0.141 BTU/lb-°F @Temperature 1830 °F |
|
| Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.590 J/g-°C @Temperature 1000 °C |
0.141 BTU/lb-°F @Temperature 1830 °F |
|
| Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.590 J/g-°C @Temperature 1000 °C |
0.141 BTU/lb-°F @Temperature 1830 °F |
|
| Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.590 J/g-°C @Temperature 1000 °C |
0.141 BTU/lb-°F @Temperature 1830 °F |
|
| Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.590 J/g-°C @Temperature 1000 °C |
0.141 BTU/lb-°F @Temperature 1830 °F |
|
| Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.590 J/g-°C @Temperature 1000 °C |
0.141 BTU/lb-°F @Temperature 1830 °F |
|
| Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.590 J/g-°C @Temperature 1000 °C |
0.141 BTU/lb-°F @Temperature 1830 °F |
|
| Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.590 J/g-°C @Temperature 1000 °C |
0.141 BTU/lb-°F @Temperature 1830 °F |
|
| Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.590 J/g-°C @Temperature 1000 °C |
0.141 BTU/lb-°F @Temperature 1830 °F |
|
| Haynes 188 alloy, plate at RT after 0 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.590 J/g-°C @Temperature 1000 °C |
0.141 BTU/lb-°F @Temperature 1830 °F |
|
| Haynes 188 alloy, plate at RT after 1000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.590 J/g-°C @Temperature 1000 °C |
0.141 BTU/lb-°F @Temperature 1830 °F |
|
| Haynes 188 alloy, plate at RT after 16000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.590 J/g-°C @Temperature 1000 °C |
0.141 BTU/lb-°F @Temperature 1830 °F |
|
| Haynes 188 alloy, plate at RT after 8000 hours at 650°C (1200°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.590 J/g-°C @Temperature 1000 °C |
0.141 BTU/lb-°F @Temperature 1830 °F |
|
| Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.590 J/g-°C @Temperature 1000 °C |
0.141 BTU/lb-°F @Temperature 1830 °F |
|
| Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.590 J/g-°C @Temperature 1000 °C |
0.141 BTU/lb-°F @Temperature 1830 °F |
|
| Haynes 188 alloy, cold rolled and 1175°C solution annealed sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.589 J/g-°C @Temperature 800 °C |
0.141 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes Hastelloy® B-3® alloy, 0% cold work The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
| Specific Heat Capacity | 0.589 J/g-°C @Temperature 800 °C |
0.141 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes Hastelloy® B-3® alloy, 20% cold work The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
| Specific Heat Capacity | 0.589 J/g-°C @Temperature 800 °C |
0.141 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes Hastelloy® B-3® alloy, 3.2 mm bright annealed sheet The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
| Specific Heat Capacity | 0.589 J/g-°C @Temperature 800 °C |
0.141 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes Hastelloy® B-3® alloy, 40% cold work The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
| Specific Heat Capacity | 0.589 J/g-°C @Temperature 800 °C |
0.141 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes Hastelloy® B-3® alloy, 6.3 mm plate The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
| Specific Heat Capacity | 0.590 J/g-°C | 0.141 BTU/lb-°F | |
| Schott N-PSK53A Glass Information Provided by SCHOTT North America, Inc. |
|||
| Specific Heat Capacity | 0.590 J/g-°C | 0.141 BTU/lb-°F | |
| Schott N-LAK21 Glass Information Provided by SCHOTT North America, Inc. |
|||
| Specific Heat Capacity | 0.589 J/g-°C @Temperature 800 °C |
0.141 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes Hastelloy® B-3® alloy, heat treated at 1065°C, rapid quenched The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and ea.. |
|||