- Polymer Property : Specific Heat Capacity = 0.133 BTU/lb-°F
Polymer Property : Specific Heat Capacity = 0.133 BTU/lb-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Heat Capacity | 0.557 J/g-°C @Temperature 800 °C |
0.133 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes 188 alloy, 0% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.557 J/g-°C @Temperature 800 °C |
0.133 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.557 J/g-°C @Temperature 800 °C |
0.133 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.557 J/g-°C @Temperature 800 °C |
0.133 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.557 J/g-°C @Temperature 800 °C |
0.133 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.557 J/g-°C @Temperature 800 °C |
0.133 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.557 J/g-°C @Temperature 800 °C |
0.133 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.557 J/g-°C @Temperature 800 °C |
0.133 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.557 J/g-°C @Temperature 800 °C |
0.133 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.557 J/g-°C @Temperature 800 °C |
0.133 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.557 J/g-°C @Temperature 800 °C |
0.133 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.557 J/g-°C @Temperature 800 °C |
0.133 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.557 J/g-°C @Temperature 800 °C |
0.133 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.557 J/g-°C @Temperature 800 °C |
0.133 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.557 J/g-°C @Temperature 800 °C |
0.133 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes 188 alloy, plate at RT after 0 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.557 J/g-°C @Temperature 800 °C |
0.133 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes 188 alloy, plate at RT after 1000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.557 J/g-°C @Temperature 800 °C |
0.133 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes 188 alloy, plate at RT after 16000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.557 J/g-°C @Temperature 800 °C |
0.133 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes 188 alloy, plate at RT after 4000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.557 J/g-°C @Temperature 800 °C |
0.133 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes 188 alloy, plate at RT after 8000 hours at 650°C (1200°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.557 J/g-°C @Temperature 800 °C |
0.133 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes 188 alloy, plate at RT after 8000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.558 J/g-°C @Temperature 500 °C |
0.133 BTU/lb-°F @Temperature 932 °F |
|
| Haynes HR-120® alloy, solution heat-treated Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
| Specific Heat Capacity | 0.558 J/g-°C @Temperature 500 °C |
0.133 BTU/lb-°F @Temperature 932 °F |
|
| Haynes HR-120® alloy, solution heat-treated aged at 1200°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
| Specific Heat Capacity | 0.558 J/g-°C @Temperature 500 °C |
0.133 BTU/lb-°F @Temperature 932 °F |
|
| Haynes HR-120® alloy, solution heat-treated aged at 1400°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
| Specific Heat Capacity | 0.558 J/g-°C @Temperature 500 °C |
0.133 BTU/lb-°F @Temperature 932 °F |
|
| Haynes HR-120® alloy, solution heat-treated aged at 1600°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
| Specific Heat Capacity | 0.558 J/g-°C @Temperature 500 °C |
0.133 BTU/lb-°F @Temperature 932 °F |
|
| Haynes HR-120® alloy, solution heat-treated aged at 1800°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
| Specific Heat Capacity | 0.557 J/g-°C @Temperature 800 °C |
0.133 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.557 J/g-°C @Temperature 800 °C |
0.133 BTU/lb-°F @Temperature 1470 °F |
|
| Haynes 188 alloy, plate at RT after 8000 hours at 760°C (1400°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Specific Heat Capacity | 0.558 J/g-°C @Temperature 500 °C |
0.133 BTU/lb-°F @Temperature 932 °F |
|
| Haynes HR-120® alloy, solution heat-treated plate Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
| Specific Heat Capacity | 0.557 J/g-°C | 0.133 BTU/lb-°F | |
| Schott F2 Glass Information Provided by SCHOTT North America, Inc. |
|||
| Specific Heat Capacity | 0.557 J/g-°C | 0.133 BTU/lb-°F | |
| Schott F2HT Glass Information Provided by SCHOTT North America, Inc. |
|||