Polymer Property : Clash Berg Stiffness Temperature = -14.8 °F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
Clash Berg Stiffness Temperature	-26.0 °C	-14.8 °F	T-10000 Torsional stiffness ASTM D1043-72(1981)
DuPont Performance Polymers Hypalon® HPG-6525 Chlorosulfonated Polyethylene Rubber, Carbon Black Filled Compound &n Carbon black compound with 100 parts Hypalon; 27.8 parts sublimed litharge dispersion; 55 parts carbon black; 55 parts aromatic process oil; 0.5 parts MTBS; and 2 parts Tetrone® A rubber accelerato..
Clash Berg Stiffness Temperature	-26.0 °C	-14.8 °F	At 69 MPa
DuPont Vamac® G Sample Compound Vulcanizate Slab Cure (10 minutes at 177°C) Vulcanizate performance test data can help end-users evaluate the potential fitness of similar compounds for their own applications.Information provided by DuPont.
Clash Berg Stiffness Temperature	-26.0 °C	-14.8 °F	T-10000 Torsional stiffness ASTM D1043-72(1981)
DuPont Performance Polymers Hypalon® 4085 Chlorosulfonated Polyethylene Rubber, Mineral Filled Compound (disc Mineral filled compound with 100 parts Hypalon; 80 parts hard clay; 4 parts magnesia; 30 parts aromatic process oil; 3 parts pentaerythritol; and 2 parts Tetrone® A rubber accelerator (from DuPont ..
Clash Berg Stiffness Temperature	-26.0 - 7.00 °C	-14.8 - 44.6 °F	Average value: -17.6 °C Grade Count:15
Overview of materials for Chlorosulfonated Polyethylene Rubber This property data is a summary of similar materials in the MatWeb database for the category "Chlorosulfonated Polyethylene Rubber". Each property range of values reported is minimum and maximum val..