DuPont Vamac® G Sample Compound Vulcanizate Slab Cure (10 minutes at 177°C)

Category Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE)
Manufacturer DuPont Packaging and Industrial Polymers
Trade Name Vamac®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Vamac® G Sample Compound Vulcanizate Slab Cure (10 minutes at 177°C).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Vulcanizate performance test data can help end-users evaluate the potential fitness of similar compounds for their own applications.Information provided by DuPont.
Mechanical Properties Metric English Comments
Hardness, Shore A 68
68
Tensile Strength, Ultimate 15.2 MPa
2200 psi
Elongation at Break 280 %
280 %
100% Modulus 0.00510 GPa
0.740 ksi
Compression Set 6.0 %
6.0 %
70 hrs at 150°C, method B, plied
12 %
12 %
168 hrs at 150°C, method B, plied
24 %
24 %
168 hrs at 177°C, method B, plied
Thermal Properties Metric English Comments
Brittleness Temperature <= -24.0 °C
<= -11.2 °F
TR-10
Clash Berg Stiffness Temperature -26.0 °C
-14.8 °F
At 69 MPa
Descriptive Properties Value Comments
Armeen® 18D 0.5 parts
DIAK No. 7(TIAC) 1.5 parts
DOTG Coaccelerator 4 parts
Naugard® 445 antioxidant 1 part
SRF Black(N774) 65 parts
Stearic Acid 1.5 parts
Vamac® G 100 parts
Vanfre® VAM 1 part