Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Shear Strength | 44.0 MPa @Temperature 140 °C |
6380 psi @Temperature 284 °F |
ILSS; prEN2563 |
Hexcel® HexPly® M35-4 80-180°C Curing Epoxy Matrix, M35-4/40%/G1089/1000 Fabric Fiber: T800H 6K 2x2 Twill, 200 g/m2Information provided by HexCel |
|||
Shear Strength | 44.0 MPa @Temperature 22.2 °C |
6380 psi @Temperature 72.0 °F |
Lap Shear Primed, 1000 hrs in Skydrol 500A at 72°F |
Hexcel® Redux® 319A High Performance Modified Epoxy Film Adhesive (0.08 psf) Redux 319 is a high performance modified epoxy film adhesive curing at 350°F. It is available in both supported and unsupported versions at areal weights between 0.03 and 0.08 psf. The supported ve.. |
|||
Shear Strength | 44.0 MPa @Temperature 22.2 °C |
6380 psi @Temperature 72.0 °F |
Lap Shear Unprimed, No conditioning of Redux 319 |
Hexcel® Redux® 319A High Performance Modified Epoxy Film Adhesive (0.08 psf) Redux 319 is a high performance modified epoxy film adhesive curing at 350°F. It is available in both supported and unsupported versions at areal weights between 0.03 and 0.08 psf. The supported ve.. |
|||
Shear Strength | 44.0 MPa @Temperature 22.2 °C |
6380 psi @Temperature 72.0 °F |
Lap Shear Unprimed, 1000 hrs in synthetic esters at 72°F |
Hexcel® Redux® 319A High Performance Modified Epoxy Film Adhesive (0.08 psf) Redux 319 is a high performance modified epoxy film adhesive curing at 350°F. It is available in both supported and unsupported versions at areal weights between 0.03 and 0.08 psf. The supported ve.. |
|||
Shear Strength | 44.0 MPa @Temperature 22.2 °C |
6380 psi @Temperature 72.0 °F |
Lap Shear Primed, 1000 hrs in synthetic esters at 72°F |
Hexcel® Redux® 319A High Performance Modified Epoxy Film Adhesive (0.08 psf) Redux 319 is a high performance modified epoxy film adhesive curing at 350°F. It is available in both supported and unsupported versions at areal weights between 0.03 and 0.08 psf. The supported ve.. |
|||
Shear Strength | 44.0 MPa @Temperature 22.2 °C |
6380 psi @Temperature 72.0 °F |
Lap Shear Unprimed, 1000 hrs in anti-icing fluid at 72°F |
Hexcel® Redux® 319A High Performance Modified Epoxy Film Adhesive (0.08 psf) Redux 319 is a high performance modified epoxy film adhesive curing at 350°F. It is available in both supported and unsupported versions at areal weights between 0.03 and 0.08 psf. The supported ve.. |
|||
Shear Strength | 44.0 MPa @Temperature 60.0 °C |
6380 psi @Temperature 140 °F |
0º Interlaminar Shear, Conditioning: 60°C-90%RH; ASTM D2344 |
Hexcel® HexPly® M47 140°C Curing Epoxy Matrix, Unidirectional Carbon Prepreg IM2-C Fibre 1947 - 38% resin weight with IM2-C 53% fiber volumeInformation provided by HexCel |
|||
Shear Strength | 44.0 MPa @Temperature 22.2 °C |
6380 psi @Temperature 72.0 °F |
Lap Shear |
Hexcel® Redux® 641K Modified epoxy film adhesive for bonding metallic and composite components Redux 641 is a high temperature modified epoxy film adhesive curing at 350°F. It is suitable for bonding metal to metal and for sandwich structures where operating temperatures are experienced up t.. |
|||
Shear Strength | 44.0 MPa @Temperature -55.0 °C |
6380 psi @Temperature -67.0 °F |
Adhered: 50 MIL (6-4 Titanium Alloy), Adhesive AF-126 (0.06 wt) |
3M Scotch-Weld™ 3901 Metal Primer 3M™ Scotch-Weld™ Metal Primer 3901 is a primer for 3M™ Scotch-Weld™ film and liquid adhesives in those applications where it is desired to obtain improved metal and glass adhesion or improved re.. |