Polymer Property : Shear Strength = 580 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Shear Strength	4.00 MPa @Temperature 120 °C	580 psi @Temperature 248 °F	Aluminum Double Lap Shear (0.06 inch gap)
Hexcel® Redux® 208/4-NA Foaming adhesive film The Redux 200 series is a range fo foaming adhesive films presented in sheet form. They expand during the cure cycle to fill gaps and adhere strongly to all parts of the structure with which they co..
Shear Strength	4.00 MPa @Temperature 23.0 °C	580 psi @Temperature 73.4 °F	Overlap, Polystyrene
3M Scotch-Weld™ TE030 Polyurethane Reactive Adhesive 3M™ Scotch-Weld™ Polyurethane Reactive Adhesives are a family of one-component, moisture curing, urethane adhesives. These adhesives are applied warm and bond a wide variety of substrates such as ..
Shear Strength	4.00 MPa @Temperature 23.0 °C	580 psi @Temperature 73.4 °F	Overlap, Polystyrene, Substrate Failure
3M Scotch-Weld™ TE031 Black Polyurethane Reactive Adhesive 3M™ Scotch-Weld™ Polyurethane Reactive Adhesives are a family of one-component, moisture curing, urethane adhesives. These adhesives are applied warm and bond a wide variety of substrates such as ..
Shear Strength	4.00 MPa @Temperature 24.0 °C	580 psi @Temperature 75.2 °F	Overlap, Nylon
3M Scotch-Weld™ 3532 B/A Two-Part Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie..
Shear Strength	4.00 MPa @Temperature 24.0 °C	580 psi @Temperature 75.2 °F	Overlap, Nylon
3M Scotch-Weld™ 3535 B/A Two-Part Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie..
Shear Strength	4.00 MPa @Temperature 24.0 °C	580 psi @Temperature 75.2 °F	Overlap, Nylon
3M Scotch-Weld™ 3549 B/A Two-Part Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie..