3M Scotch-Weld™ TE030 Polyurethane Reactive Adhesive

Category	Polymer , Adhesive
Manufacturer	3M
Trade Name	Scotch-Weld™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	3M Scotch-Weld™ TE030 Polyurethane Reactive Adhesive.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

3M™ Scotch-Weld™ Polyurethane Reactive Adhesives are a family of one-component, moisture curing, urethane adhesives. These adhesives are applied warm and bond a wide variety of substrates such as wood, fiber reinforced plastic (FRP) and many other plastics to themselves, to metal and glass. Extrudable grade with fast set time ideal for bonding wood. Also bonds selected plastics.Information provided by 3M

Physical Properties	Metric	English	Comments
Density	1.04 g/cc	0.0376 lb/in³
Brookfield Viscosity	16000 cP	16000 cP	Thermosel using spindle #27

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	60	60
Tensile Strength at Break	26.2 MPa	3800 psi	ASTM D638 Die C
Elongation at Break	725 %	725 %	ASTM D638 Die C
Tensile Modulus	0.0772 GPa	11.2 ksi	ASMT D638 Die C
Shear Strength	3.03 MPa @Temperature 82.0 °C	440 psi @Temperature 180 °F	Overlap, Maple
	4.00 MPa @Temperature 23.0 °C	580 psi @Temperature 73.4 °F	Overlap, Polystyrene
	4.48 MPa @Temperature 23.0 °C	650 psi @Temperature 73.4 °F	Overlap, Polyacrylic
	5.31 MPa @Temperature 23.0 °C	770 psi @Temperature 73.4 °F	Overlap, ABS
	6.00 MPa @Temperature 82.0 °C	870 psi @Temperature 180 °F	Overlap, FRP
	12.1 MPa @Temperature 23.0 °C	1750 psi @Temperature 73.4 °F	Overlap, Polycarbonate
	12.1 MPa @Temperature 23.0 °C	1760 psi @Temperature 73.4 °F	Overlap, PVC, Substrate Failure
	13.0 MPa @Temperature 23.0 °C	1890 psi @Temperature 73.4 °F	Overlap, Maple
	16.4 MPa @Temperature 23.0 °C	2380 psi @Temperature 73.4 °F	Overlap, FRP
Peel Strength	1.93 kN/m	11.0 pli	T-Peel, Initial, Substrate failure
	2.28 kN/m	13.0 pli	180°, Polyacrylic
	2.98 kN/m	17.0 pli	T-Peel, Aged 71°C for 2 weeks, Substrate failure
	9.64 kN/m	55.0 pli	180°, Polycarbonate
	9.64 kN/m	55.0 pli	180°, ABS
	12.3 kN/m	70.0 pli	180°, PVC, Cotton duck failed during testing
	14.7 kN/m	84.0 pli	180°, FRP, Cotton duck failed during testing

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	121 °C	250 °F

Processing Properties	Metric	English	Comments
Cure Time	0.500 min	0.00833 hour	Set Time

Descriptive Properties	Value	Comments
Appearance	White/Off-White