Polymer Property : Flexural Strength = 89.6 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	89.6 MPa @Temperature 232 °C	13000 psi @Temperature 450 °F	ASTM D790
Solvay Specialty Polymers Torlon® 4435 Polyamide-imide (PAI) (Unverified Data**) Torlon 4435 is a polyamide-imide resin specifically designed to provide exceptionally low wear performance in non-lubricated applications even at high pressure and velocity (PV) conditions. Not only..
Flexural Strength	89.6 MPa @Thickness 1.57 mm	13000 psi @Thickness 0.0620 in	CW; ASTM D790
Industrial Laminates/Norplex NP193M Synthetic Fabric Base Grade Description: 17 oz. aramide and â€œsoft glassâ€ fibers are combined to make a fabric that is stronger than pure aramide and less abrasive than glass fabrics. This material is impregnated with..
Flexural Strength	89.6 MPa @Thickness 1.57 mm	13000 psi @Thickness 0.0620 in	CW; ASTM D790
Industrial Laminates/Norplex NP691 Paper Base Laminate Description: Flame resistant, room temperature punching grade. NP691 is very similar to NP612 in electrical properties and mechanical strength, with improved moisture resistance.Thickness Tested: 0...
Flexural Strength	89.6 MPa @Temperature 232 Â°C	13000 psi @Temperature 450 Â°F	ASTM D790
Solvay Specialty Polymers TorlonÂ® 4435 Polyamide-imide (PAI) TorlonÂ® 4435 is a polyamide-imide resin specifically designed to provide exceptionally low wear performance in non-lubricated applications even at high pressure and velocity (PV) conditions. Not ..
Flexural Strength	89.6 MPa @Temperature 23.9 Â°C	13000 psi @Temperature 75.0 Â°F	ASTM D790
Saint-Gobain MeldinÂ® 7022 CM Compression Molded Graphite Filled Polyimide MelidinÂ® 7022 CM is a compression molded polyimide that contains 40% graphite filler. This grade offers additional dimensional stability at elevated temperatures and the lowest CTE of any Meldin..