Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Modulus of Rupture | 0.00210 GPa @Temperature 540 °C |
0.305 ksi @Temperature 1000 °F |
Fired; ASTM C268 |
BNZ Materials Blazecrete 2500 HS Dense Castable Blazecrete 2500 HSis a high-duty castable designed to withstand loads and resist normal abrasion and erosion at moderate temperatures to 2500°F (1371°C). Use with Blaz 2100 for a dual component li.. |
|||
Modulus of Rupture | 0.00210 GPa @Temperature 815 °C |
0.305 ksi @Temperature 1500 °F |
ASTM C268 |
BNZ Materials Blazecrete 2500 HS Dense Castable Blazecrete 2500 HSis a high-duty castable designed to withstand loads and resist normal abrasion and erosion at moderate temperatures to 2500°F (1371°C). Use with Blaz 2100 for a dual component li.. |
|||
Modulus of Rupture | 0.00210 GPa @Temperature 1260 °C |
0.305 ksi @Temperature 2300 °F |
ASTM C268 |
BNZ Materials Blazecrete 2500 HS Dense Castable Blazecrete 2500 HSis a high-duty castable designed to withstand loads and resist normal abrasion and erosion at moderate temperatures to 2500°F (1371°C). Use with Blaz 2100 for a dual component li.. |
|||
Modulus of Rupture | 0.00210 GPa @Temperature 540 °C |
0.305 ksi @Temperature 1000 °F |
Fired; ASTM C268 |
BNZ Materials Blazecrete 2300 ARG Dense Castable Blazecrete 2300 ARG is an alumina-silica castable with high strength and abrasion resistance. For service to 2300°F (1260°C). May be gunned or slap-troweled over Blaz 2000G to obtain a high streng.. |
|||
Modulus of Rupture | 0.00210 GPa @Temperature 815 °C |
0.305 ksi @Temperature 1500 °F |
ASTM C268 |
BNZ Materials Blazecrete 2300 ARG Dense Castable Blazecrete 2300 ARG is an alumina-silica castable with high strength and abrasion resistance. For service to 2300°F (1260°C). May be gunned or slap-troweled over Blaz 2000G to obtain a high streng.. |
|||
Modulus of Rupture | 0.00210 GPa @Temperature 1260 °C |
0.305 ksi @Temperature 2300 °F |
ASTM C268 |
BNZ Materials Blazecrete 2300 ARG Dense Castable Blazecrete 2300 ARG is an alumina-silica castable with high strength and abrasion resistance. For service to 2300°F (1260°C). May be gunned or slap-troweled over Blaz 2000G to obtain a high streng.. |