BNZ Materials Blazecrete 2300 ARG Dense Castable

Category Ceramic , Oxide , Silicon Oxide
Manufacturer BNZ Materials, Inc.
Trade Name Blazecrete
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BNZ Materials Blazecrete 2300 ARG Dense Castable.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Blazecrete 2300 ARG is an alumina-silica castable with high strength and abrasion resistance. For service to 2300°F (1260°C). May be gunned or slap-troweled over Blaz 2000G to obtain a high strength hot face with a good insulating back-up. Suitable for ash pits, dust collector flues and other areas where abrasive or erosive conditions exist.Information provided by BNZ Materials Inc.
Physical Properties Metric English Comments
Density 1.92 g/cc
0.0694 lb/in³
Mechanical Properties Metric English Comments
Modulus of Rupture 0.00140 GPa

@Temperature 1095 °C
0.203 ksi

@Temperature 2003 °F
ASTM C268
0.00210 GPa

@Temperature 540 °C
0.305 ksi

@Temperature 1000 °F
Fired; ASTM C268
0.00210 GPa

@Temperature 815 °C
0.305 ksi

@Temperature 1500 °F
ASTM C268
0.00210 GPa

@Temperature 1260 °C
0.305 ksi

@Temperature 2300 °F
ASTM C268
0.00760 GPa

@Temperature 104 °C
1.10 ksi

@Temperature 219 °F
Dried; ASTM C268
Compressive Strength 16.5 MPa

@Temperature 1095 °C
2390 psi

@Temperature 2003 °F
Cold Crush Strength
17.9 MPa

@Temperature 1260 °C
2600 psi

@Temperature 2300 °F
Cold Crush Strength
24.1 MPa

@Temperature 815 °C
3500 psi

@Temperature 1500 °F
Cold Crush Strength
22.4 MPa

@Treatment Temp. 540 °C
3250 psi

@Treatment Temp. 1000 °F
Cold Crush Strength; Dried 104°C
48.9 MPa

@Treatment Temp. 104 °C
7090 psi

@Treatment Temp. 219 °F
Cold Crush Strength; Dried 104°C
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 1260 °C
2300 °F
Shrinkage 0.10 %

@Temperature 104 °C
0.10 %

@Temperature 219 °F
Permanent Linear Change; ASTM C210
0.20 %

@Temperature 540 °C
0.20 %

@Temperature 1000 °F
Permanent Linear Change; ASTM C210
0.30 %

@Temperature 815 °C
0.30 %

@Temperature 1500 °F
Permanent Linear Change; ASTM C210
0.30 %

@Temperature 1095 °C
0.30 %

@Temperature 2003 °F
Permanent Linear Change; ASTM C210
1.1 %

@Temperature 1260 °C
1.1 %

@Temperature 2300 °F
Permanent Linear Change; ASTM C210
Component Elements Properties Metric English Comments
Al2O3 33.4 %
33.4 %
CaO 13.6 %
13.6 %
Fe2O3 7.9 %
7.9 %
Na2O 0.10 %
0.10 %
Includes K<sub>2</sub>O
SiO2 40.2 %
40.2 %
TiO2 1.0 %
1.0 %