Polymer Property : Flexural Modulus = 453 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Modulus	3.12 GPa	453 ksi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Lexan® 500ECR PC Lexan* 500ECR Polycarbonate (PC) resin is a 10% glass fiber filled, injection moldable grade. It is of non-chlorinated & non-brominated flame retardant systems with UL-94 V0 rating at 2.3mm. It is a..
Flexural Modulus	3.12 GPa	453 ksi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Lexan® 500ECR PC (Asia Pacific) Lexan* 500ECR Polycarbonate (PC) resin is a 10% glass fiber filled, injection moldable grade. It is of non-chlorinated & non-brominated flame retardant systems with UL-94 V0 rating at 2.3mm. It is a..
Flexural Modulus	3.12 GPa	453 ksi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Lexan® 500ECR PC (Europe-Africa-Middle East) Lexan* 500ECR Polycarbonate (PC) resin is a 10% glass fiber filled, injection moldable grade. It is of non-chlorinated & non-brominated flame retardant systems with UL-94 V0 rating at 2.3mm. It is a..
Flexural Modulus	3.12 GPa	453 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP LL002 PEEK LNP* LUBRICOMP* LL002 is a compound based on Polyetheretherketone containing 10% PTFE. Added feature of this material is: Wear Resistant.
Flexural Modulus	3.12 GPa	453 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOCOMP NF001 PC+ABS LNP THERMOCOMP* NF001 is a compound based on PC+ABS resin containing 5% Glass Fiber.
Flexural Modulus	3.12 GPa	453 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOCOMP NF001XXX PC+ABS LNP* THERMOCOMP* PCA-F-1001 is a compound based on PC+ABS resin containing 5% Glass Fiber.
Flexural Modulus	3.12 GPa	453 ksi	ISO 178
Hexcel® HexPly® 924 180°C Curing Epoxy Matrix HexPly® 924 is a controlled flow epoxy matrix developed for the fabrication of high temperature resistant primary structures. When cured, HexPly® 924 becomes a tough composite with high impact res..
Flexural Modulus	3.12 GPa	453 ksi	50%RH; ISO 178
DuPont Performance Polymers Zytel® 80G14AHS NC010 Nylon 66 (Unverified Data**) 14% Glass Reinforced Toughened Heat Stabilized Polyamide 66 Zytel 80G14AHS NC010 is a 14% glass fiber reinforced toughened high flow heat stabilized polyamide 66 resin. It offers outstanding perform..