SABIC Innovative Plastics Lexan® 500ECR PC

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® 500ECR PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Lexan* 500ECR Polycarbonate (PC) resin is a 10% glass fiber filled, injection moldable grade. It is of non-chlorinated & non-brominated flame retardant systems with UL-94 V0 rating at 2.3mm. It is available in various opaque color options designed for applications requiring improved stiffness.
Physical Properties Metric English Comments
Specific Gravity 1.27 g/cc
1.27 g/cc
ASTM D792
Density 1.25 g/cc
0.0452 lb/in³
ISO 1183
Moisture Absorption 0.130 %
0.130 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.31 %
0.31 %
ISO 62
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm

@Thickness 3.20 mm
0.0040 - 0.0060 in/in

@Thickness 0.126 in
SABIC Method
Linear Mold Shrinkage, Transverse 0.0040 - 0.0060 cm/cm

@Thickness 3.20 mm
0.0040 - 0.0060 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 7.5 g/10 min

@Load 1.20 kg,
Temperature 300 °C
7.5 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D1238
Melt Index of Compound 7.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
7.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Hardness, H358/30 115 MPa
16700 psi
ISO 2039-1
Tensile Strength at Break 45.0 MPa
6530 psi
5 mm/min; ISO 527
48.0 MPa
6960 psi
Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield 57.0 MPa
8270 psi
Type I, 5 mm/min; ASTM D638
60.0 MPa
8700 psi
5 mm/min; ISO 527
Elongation at Break 7.0 %
7.0 %
5 mm/min; ISO 527
46 %
46 %
Type I, 5 mm/min; ASTM D638
Elongation at Yield 4.7 %
4.7 %
Type I, 5 mm/min; ASTM D638
5.0 %
5.0 %
5 mm/min; ISO 527
Tensile Modulus 2.46 GPa
357 ksi
5 mm/min; ASTM D638
3.30 GPa
479 ksi
1 mm/min; ISO 527
Flexural Strength 94.0 MPa
13600 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Yield Strength 95.0 MPa
13800 psi
2 mm/min; ISO 178
Flexural Modulus 3.12 GPa
453 ksi
1.3 mm/min, 50 mm span; ASTM D790
3.40 GPa
493 ksi
2 mm/min; ISO 178
Izod Impact, Notched 1.34 J/cm
2.51 ft-lb/in
ASTM D256
1.00 J/cm

@Temperature -30.0 °C
1.87 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Unnotched NB

@Thickness 6.40 mm
NB

@Thickness 0.252 in
ASTM D4812
Izod Impact, Notched (ISO) 10.0 kJ/m²
4.76 ft-lb/in²
80*10*3; ISO 180/1A
8.00 kJ/m²

@Temperature -30.0 °C
3.81 ft-lb/in²

@Temperature -22.0 °F
80*10*3; ISO 180/1A
Izod Impact, Unnotched (ISO) NB
NB
80*10*3; ISO 180/1U
NB
NB
80*10*4; ISO 180/1U
130 kJ/m²

@Temperature -30.0 °C
61.9 ft-lb/in²

@Temperature -22.0 °F
80*10*3; ISO 180/1U
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
80*10*4; ISO 180/1U
Charpy Impact Unnotched NB
NB
Edgew 80*10*4 sp=62mm; ISO 179/1eU
NB
NB
Edgew 80*10*3 sp=62mm; ISO 179/1eU
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eU
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
Edgew 80*10*4 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 0.900 J/cm²
4.28 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
1.00 J/cm²
4.76 ft-lb/in²
Edgew 80*10*3 sp=62mm; ISO 179/1eA
1.50 J/cm²
7.14 ft-lb/in²
ISO 179/2C
0.900 J/cm²

@Temperature -30.0 °C
4.28 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 61.0 J

@Temperature 23.0 °C
45.0 ft-lb

@Temperature 73.4 °F
ASTM D3763
Taber Abrasion, mg/1000 Cycles 11
11
CS-17, 1 kg; SABIC Method
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 40.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
22.2 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-2
46.8 µm/m-°C

@Temperature -40.0 - 40.0 °C
26.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 84.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
47.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
84.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
47.0 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Thermal Conductivity 0.210 W/m-K
1.46 BTU-in/hr-ft²-°F
ISO 8302
Deflection Temperature at 0.46 MPa (66 psi) 144 °C
291 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
143 °C

@Thickness 3.20 mm
289 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 136 °C
277 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
136 °C
277 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
142 °C
288 °F
Annealed 120°C, 2hrs; ISO 75/Ae
136 °C

@Thickness 3.20 mm
277 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 141 °C
286 °F
Rate B/50; ISO 306
143 °C
289 °F
Rate B/120; ISO 306
154 °C
309 °F
Rate B/50; ASTM D1525
UL RTI, Electrical 130 °C
266 °F
UL 746B
UL RTI, Mechanical with Impact 130 °C
266 °F
UL 746B
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ROA; IEC 60093
Dielectric Constant 2.8

@Frequency 1.00e+6 Hz
2.8

@Frequency 1.00e+6 Hz
IEC 60250
2.9

@Frequency 50.0 - 60.0 Hz
2.9

@Frequency 50.0 - 60.0 Hz
IEC 60250
Dielectric Strength 16.0 kV/mm

@Thickness 3.20 mm
406 kV/in

@Thickness 0.126 in
in oil; IEC 60243-1
25.0 kV/mm

@Thickness 1.60 mm
635 kV/in

@Thickness 0.0630 in
in oil; IEC 60243-1
33.0 kV/mm

@Thickness 0.800 mm
838 kV/in

@Thickness 0.0315 in
in oil; IEC 60243-1
Dissipation Factor 0.0010

@Frequency 50.0 - 60.0 Hz
0.0010

@Frequency 50.0 - 60.0 Hz
IEC 60250
0.010

@Frequency 1.00e+6 Hz
0.010

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 150 V
150 V
IEC 60112
175 - 250 V
175 - 250 V
UL 746A
Hot Wire Ignition, HWI 7.0 - 15 sec
7.0 - 15 sec
UL 746A
High Amp Arc Ignition, HAI 0.00 - 15 arcs
0.00 - 15 arcs
UL 746A