Polymer Property : Flexural Modulus = 4.68 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Modulus	4.68 GPa	679 ksi	ISO 178
FKuR Kunststoff Bio-FlexÂ® S 9533 Compostable PLA Blend The BIO-FLEXÂ® trade name indicates blends of co-polyester and PLA* with, depending on the particular grade, a very high content of natural resource material. BIO-FLEXÂ® does not contain any sta..
Flexural Modulus	4.68 GPa	679 ksi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics ValoxÂ® EH7020HF PBT+PET Valox EH7020HF is a mineral filled PBT/PET that offers good surface appearance, high flow and good heat performance. EH7020HF was developed for automotive bezel application that requires basecoat + ..
Flexural Modulus	4.68 GPa	679 ksi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics ValoxÂ® EH7020HF PBT+PET (Asia Pacific) Valox EH7020HF is a mineral filled PBT/PET that offers good surface appearance, high flow and good heat performance. EH7020HF was developped for automotiove bezel application that require basecoat +..
Flexural Modulus	4.68 GPa	679 ksi	ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP DF0029P PC LNP THERMOCOMP* DF0029P is a compound based on Polycarbonate resin containing 10% Glass Fiber. Added features of this material include: Exceptional Processing. Flame Retardant.
Flexural Modulus	4.68 GPa	679 ksi	ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP JF002 PES (Asia Pacific) LNP THERMOCOMP* JF002 is a compound based on Polyethersulfone resin containing Glass Fiber.
Flexural Modulus	4.68 GPa	679 ksi	ASTM D 790
SABIC Innovative Plastics LNP Thermocomp JX89569 PES LNP THERMOCOMP* JX89569 is a compound based on Polyethersulfone resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region.
Flexural Modulus	4.68 GPa	679 ksi	ASTM D 790
SABIC Innovative Plastics LNP Thermocomp JX89569 PES (Asia Pacific) LNP* THERMOCOMP* JX89569 is a compound based on Polyethersulfone resin containing Glass Fiber.This data was supplied by SABIC-IP for the Asia Pacific region.