Polymer Property : Flexural Modulus = 3.27 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Modulus	3.27 GPa @Thickness 3.20 mm	474 ksi @Thickness 0.126 in	15mm/min; ASTM D790
LG Chemical GPPS 25SP(E) PS, High Transparency, Heat Resistance Description: Injection Molding, PS, High Transparency, Heat ResistanceApplication: PSP, Food Tray, Electric/Electrical Component, CoatingCAS: 9003-53-6Information provided by LG Chemical
Flexural Modulus	3.27 GPa @Thickness 3.20 mm	474 ksi @Thickness 0.126 in	15mm/min; ASTM D790
LG Chemical GPPS 25SP(I) PS, High Transparency, Heat Resistance Description: Injection Molding, PS, High Transparency, Heat ResistanceApplication: PSP, Food Tray, Electric/Electrical Component, CoatingCAS: 9003-53-6Information provided by LG Chemical
Flexural Modulus	3.27 GPa	474 ksi	2 mm/min, 64mm span; ISO 178
SABIC Innovative Plastics SABIC PPCOMPOUND 55T1040 PP SABICÂ® PPcompound 55T1040 is a general purpose, talc filled, heat stabilized copolymer polypropylene compound. This compound exhibits very high impact and high rigidity, and is suitable for injec..
Flexural Modulus	3.27 GPa	474 ksi	ISO 178
SABIC Innovative Plastics LNP LUBRICOMP RL0019 PA 66 LNP LUBRICOMP* RL0019 is a compound based on Nylon 66 resin containing 5% PTFE. Added features of this material include: Flame Retardant, Wear Resistant.
Flexural Modulus	3.27 GPa	474 ksi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP RX05487 PA 66 LNP* LUBRICOMP* RX05487 is a compound based on Nylon 66 containing 10% Aramid Fiber, 10% Lubricant. Added features of this material are: Low Warpage, Wear Resistant.
Flexural Modulus	3.27 GPa	474 ksi	ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP AX08306 ABS (Asia Pacific) LNP* Thermocomp* AX08306 is a compound based on Acrylonitrile Butadiene Styrene resin containing Mineral.
Flexural Modulus	3.27 GPa	474 ksi	ASTM D 790
SABIC Innovative Plastics LNP Thermotuf VF002 PA 66 LNP THERMOTUF* VF002 is a compound based on Nylon resin containing Glass Fiber. Added features of this material include: High Impact.This data was supplied by SABIC-IP for the Americas region.
Flexural Modulus	3.27 GPa	474 ksi	ASTM D 790
SABIC Innovative Plastics LNP Thermotuf VF002 PA 66 (Asia Pacific) LNP THERMOTUF* VF002 is a compound based on Nylon resin containing Glass Fiber. Added features of this material include: High Impact.This data was supplied by SABIC-IP for the Asia Pacific region.
Flexural Modulus	3.27 GPa	474 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOCOMP WF002I PBT LNP* THERMOTUF* WF006I is a compound based on PBT resin containing 10% Glass Fiber. Added feature of this grade is: High Impact.