SABIC Innovative Plastics LNP THERMOCOMP WF002I PBT

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP WF002I PBT.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* THERMOTUF* WF006I is a compound based on PBT resin containing 10% Glass Fiber. Added feature of this grade is: High Impact.
Physical Properties Metric English Comments
Specific Gravity 1.32 g/cc
1.32 g/cc
ASTM D792
Density 1.32 g/cc
0.0477 lb/in³
ASTM D792
Moisture Absorption 0.0700 %
0.0700 %
50% RH, 24 hrs; ASTM D570
0.100 %
0.100 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow >= 0.020 cm/cm

@Time 86400 sec
>= 0.020 in/in

@Time 24.0 hour
ASTM D955
Linear Mold Shrinkage, Transverse 0.010 - 0.030 cm/cm

@Time 86400 sec
0.010 - 0.030 in/in

@Time 24.0 hour
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 55.0 MPa
7980 psi
Type I, 5 mm/min; ASTM D638
60.0 MPa
8700 psi
5 mm/min; ISO 527
Tensile Strength, Yield 62.0 MPa
8990 psi
5 mm/min; ISO 527
64.0 MPa
9280 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 4.3 %
4.3 %
5 mm/min; ISO 527
4.4 %
4.4 %
Type I, 5 mm/min; ASTM D638
Elongation at Yield 3.4 %
3.4 %
5 mm/min; ISO 527
3.4 %
3.4 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 3.67 GPa
532 ksi
1 mm/min; ISO 527
3.77 GPa
547 ksi
5 mm/min; ASTM D638
Flexural Strength 102 MPa
14800 psi
ISO 178
Flexural Yield Strength 102 MPa
14800 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 3.27 GPa
474 ksi
2 mm/min; ISO 178
3.32 GPa
482 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 1.25 J/cm
2.34 ft-lb/in
ASTM D256
Izod Impact, Unnotched 7.08 J/cm
13.3 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 11.0 kJ/m²
5.23 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 39.0 kJ/m²
18.6 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 6.00 J

@Temperature 23.0 °C
4.43 ft-lb

@Temperature 73.4 °F
ASTM D3763
Impact Test 1.00 J
0.738 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 72.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
40.0 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D696
CTE, linear, Transverse to Flow 111 µm/m-°C

@Temperature -30.0 - 30.0 °C
61.7 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 207 °C
405 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
214 °C

@Thickness 3.20 mm
417 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 161 °C
322 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
178 °C

@Thickness 3.20 mm
352 °F

@Thickness 0.126 in
unannealed; ASTM D648