Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Rupture Strength | 97.0 MPa @Temperature 815 °C, Time 360000 sec |
14100 psi @Temperature 1500 °F, Time 100 hour |
Initial Stress |
Haynes X-750 Nickel Alloy Sheet and Strip (AMS 5598, UNS N07750) Haynes X-750 (UNS No. N07750) alloy is an age-hardenable, nickel-base superalloy with very good strength at temperatures up to about 1600°F (870°C). It is widely used as a wrought material for.. |
|||
Rupture Strength | 97.0 MPa @Temperature 871 °C, Time 3.60e+6 sec |
14100 psi @Temperature 1600 °F, Time 1000 hour |
Plate |
Haynes 282® Nickel Alloy Sheet, Plate and Bar, Solution Annealed Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and la.. |