Polymer Property : Tensile Strength, Ultimate = 972 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	972 MPa	141000 psi
Haynes HastelloyÂ® C-22Â® alloy, 10% cold worked sheet, aged 100 hours at 500Â°C HASTELLOYÂ® C-22Â® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an..
Tensile Strength, Ultimate	972 MPa	141000 psi	13"x11", 700Â°F
Latrobe LescalloyÂ® 6305 VAC-ARC ; High Strength Alloy Steel LESCALLOY 6305 VAC-ARC steel is a modified 4140 steel with higher molybdenum and a vanadium addition. The alloy steel is generally used in the 160/180,000 psi tensile strength range obtained with a..
Tensile Strength, Ultimate	972 MPa	141000 psi
Special Metals INCONELÂ® 625LCFÂ® Nickel Superalloy (UNS N06626) Annealed + 40% Cold Work Tensile strength (ultimate and yield), elongation, and reduction of area values are for annealed then cold worked samples. This produces ASTM grain size 10.0. Other property values are typical of ..
Tensile Strength, Ultimate	972 - 1030 MPa	141000 - 149000 psi	Rm
Arcam Ti6Al4V Titanium Alloy Ti6Al4V is the most widely used titanium alloy and has numerous applications in the medical industry, aerospace, automotive and marine equipment industry. Ti6Al4V ELI features Extra Low Interstitial..
Tensile Strength, Ultimate	972 MPa	141000 psi
Carpenter Gall-Tough PLUS™ Stainless, Annealed, 20% Cold Work Data provided by Carpenter Technology Corporation.Annealed 1150°C, water quenched, and cold drawn.Threshold Galling Stress 48 MPa. The avg. total volume loss on the wear test is 10.6 mm³ at 100 r..