Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 67.0 MPa | 9720 psi | ASTM D638 |
Plaskolite Optix® CA-81 General Purpose Acrylic Resin Extrusion Grade Pellets. Highest Molecular weight. |
|||
Tensile Strength, Ultimate | 67.0 MPa | 9720 psi | ASTM D638 |
Plaskolite West Optix® CA-81 General Purpose Acrylic Resin Extrusion Grade Pellets. Highest Molecular weight. |
|||
Tensile Strength, Ultimate | 67.0 MPa | 9720 psi | 5 mm/min |
Polimeri Europa KOSTIL B266 Styrene Acrylonitrile Symbol according to ISO 1043-1: SAN Grade designation according to ISO 4894-SAN 2,M,105-15 Standard injection moulding grade with good chemical resistance Application fields: household and small .. |
|||
Tensile Strength, Ultimate | 67.0 MPa | 9720 psi | |
Polycasa Acryl® G 66 Acrylic, Injection Molding Grade Injection molding grade used for: Fresnel lenses, filter screens for TVs and VDUs, drawing instruments.Data was collected by ISO methods.Quinn Manufacturing Group rebranded its Plastics Division as .. |
|||
Tensile Strength, Ultimate | 67.0 MPa | 9720 psi | 5 mm/min; parallel to flow; ASTM D638 |
Asahi Kasei Tenac® 2013A Acetal Homopolymer, UV Stabilized
(discontinued **) Similar to 3013A, but higher in molecular weight.Applications: Pipe fittings, rollers, exterior automotive parts.This product is not a part of the standard product line dated 2003. |
|||
Tensile Strength, Ultimate | 67.0 MPa | 9720 psi | 5 mm/min (0.2 in/min) |
Aardvark Polymers AARTEL® 2100UV Acetal Homopolymer Rotational Molding Resin Aartel 2100UV is a natural acetal homopolymer with UV stabilizers.Aartel 2100UV is a medium viscosity resin with excellent flow characteristics.Aartel 2100UV is available in natural white and may be.. |
|||
Tensile Strength, Ultimate | 67.0 MPa | 9720 psi | |
Lucite International Lucite® 30B Acrylic Bead Resin Lucite® 30B is usually compression molded and is a high flow methyl methacrylate copolymer.General Lucite® Acrylic Bead Resin Information: Used in casting and embedment, compression molding, d.. |
|||
Tensile Strength, Ultimate | 67.0 MPa | 9720 psi | cond; ISO 527-1/-2 |
DSM Novamid® 1013GMF H2 NAT/BK37 PA6-GF30 30% Glass Reinforced, Heat Stabilized, Injection Molding, Excellent Dimensional Stability |
|||
Tensile Strength, Ultimate | 67.0 MPa | 9720 psi | 5 mm/min |
Arkema Group Orgalloy® RS 66M25 Nylon 66 Alloy, 25% Mineral Filled (Conditioned) RS 66 series, rigid polyamide 66 alloy: easy to process, chemical resistance (no known solvents) and low moisture absorption leading to stability of mechanical, electrical and dimensional propertie.. |
|||
Tensile Strength, Ultimate | 67.0 MPa | 9720 psi | 5mm/min; ISO 527 |
BASF Ultramid® 8267G HS BK-102 15/25% Glass/Mineral Filled PA6 (Conditioned) Ultramid 8267G HS BK-102 is a heat stabilized, black pigmented, 40% mineral and glass fiber reinforced nylon 6 injection molding compound. It possesses a balance of engineering properties in combin.. |
|||
Tensile Strength, Ultimate | 67.0 MPa | 9720 psi | ATSM D638 |
Ashley Polymers Ashlene® P292 PPO Extrusion grade, highest heat deflection temperature and good impact strength.Data provided by the manufacturer |
|||
Tensile Strength, Ultimate | 67.0 MPa | 9720 psi | ASTM D638 |
A. Schulman ComAlloy Hiloy® 119 Polypropylene, Glass/Mineral Reinforced, Chemically Coupled Data provided by the manufacturer, ComAlloy International Company.30% Glass/Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Tensile Strength, Ultimate | 67.0 MPa @Thickness 2.00 mm |
9720 psi @Thickness 0.0787 in |
molded plaque, cured 20 hr at 100°C; ASTM D412 |
BASF Elastollan® C85A10 (917) Wire & Cable Grade Polyurethane Elastomer As with all TPU products this grade must be dried prior to processing.Information provided by BASF Corporation. |
|||
Tensile Strength, Ultimate | 67.0 MPa @Temperature 120 °C |
9720 psi @Temperature 248 °F |
ISO 527 |
LATI LASULF G/20 20% Glass Reinforced Polysulfone (PSU)
(Unverified Data**) Description: Lasulf products are composed of polysulfone (PSU). They feature good thermal and mechanical properties such as excellent toughness, even at low temperatures, excellent dimensional stabi.. |
|||
Tensile Strength, Ultimate | 67.0 MPa | 9720 psi | ISO 527 |
LATI LARIL 13-V1 Polyphenylene Oxide (PPOm) (UL94V-1)
(discontinued **) Description: Laril thermoplastics are polyphenylene oxide (PPOm) products. They exhibit excellent toughness, even at low temperatures, good thermal resistance and dimensional stability are the most .. |
|||
Tensile Strength, Ultimate | 67.0 MPa | 9720 psi | 5mm/min; ISO 527 |
BASF Ultramid® SEGM35 H1 BK-126 15/25% Glass/Mineral Filled PA6 (Conditioned) Ultramid SEGM35 H1 BK-126 is a 40% glass/mineral reinforced injection molding grade. It offers enhanced surface appearance, it also exhibits similar UV weathering characteristics compared to 8267G .. |