Polymer Property : Tensile Strength, Ultimate = 60.8 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	60.8 MPa	8820 psi	5 mm/min; parallel to flow; ASTM D638
Asahi Kasei Tenac®-C 4510 Acetal Copolymer, General Purpose (discontinued **) General-purpose grade, characterized by balanced flowability and mechanical properties.Applications: Gears, cams, hose joints, clips, switches, mechanical parts of audio and video equipment.This pro..
Tensile Strength, Ultimate	60.8 MPa	8820 psi	5 mm/min; parallel to flow; ASTM D638
Asahi Kasei Tenac®-C 7510 Acetal Copolymer, High Flow (discontinued **) High-flow grade, suited for thin-wall, long-flow-distance moldings.Applications: Lighters, aerosol bottles, fasteners.This product is not a part of the standard product line dated 2003.
Tensile Strength, Ultimate	60.8 MPa	8820 psi	ASTM Data
Styron CALIBREâ„¢ 5101 15 Polycarbonate, 10% Glass Reinforced CALIBRE 5101 is a 10% glass reinforced polycarbonate resin containing mold release for optimal processing. CALIBRE 5101 resin exhibits high modulus and excellent dimensional stability. CALIBRE 5101 ..
Tensile Strength, Ultimate	60.8 MPa	8820 psi	5mm/min; ASTM D638
Asia International Enterprise (Hong Kong) 3010F Polybutylene terephthalate Information provided by Asia International Enterprise (Hong Kong) Ltd.
Tensile Strength, Ultimate	60.8 MPa	8820 psi	5mm/min; ASTM D638
Asia International Enterprise (Hong Kong) 3010FW Polybutylene terephthalate Information provided by Asia International Enterprise (Hong Kong) Ltd.
Tensile Strength, Ultimate	60.8 MPa	8820 psi	5 mm/min; parallel to flow; ASTM D638
Asahi Kasei Tenac®-C EX351 Acetal Copolymer, Extrusion Grade (discontinued **) High-viscosity grade amenable to extrusion.Applications: Extruded rods and sheets.This product is not a part of the standard product line dated 2003.