Polymer Property : Tensile Strength, Ultimate = 525 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	>= 3.62 MPa	>= 525 psi	ASTM D412
Multibase Multi-Flex® TPE A 6221 M BLK The burn rate is 1 in/min (25 mm/min) based on ASTM FM VSS 302. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase.
Tensile Strength, Ultimate	>= 3.62 MPa	>= 525 psi	ASTM D638-95
Multibase Multi-Flex® TPO D 6006 Grey Data provided by Multibase.
Tensile Strength, Ultimate	>= 3.62 MPa	>= 525 psi	ASTM D412
Multibase Multi-FlexÂ® TPE A 5002 BLK The burn rate is 1 in/min (25 mm/min) based on ASTM FM VSS 302. Multi-Flex TPE contains Kratonâ„¢ G.Data provided by Multibase.
Tensile Strength, Ultimate	>= 3.62 MPa	>= 525 psi	ASTM D412
Multibase Multi-FlexÂ® TPE A 6006 GREY Multi-Flex TPE contains Kratonâ„¢ G.Data provided by Multibase.
Tensile Strength, Ultimate	>= 3.62 MPa	>= 525 psi	ASTM D412
Multibase Multi-FlexÂ® TPE A 6221 C GREY The burn rate is 1 in/min (25 mm/min) based on ASTM FM VSS 302. Multi-Flex TPE contains Kratonâ„¢ G.Data provided by Multibase.
Tensile Strength, Ultimate	>= 3.62 MPa	>= 525 psi	ASTM D412
Multibase Multi-FlexÂ® TPE A 6221 CU GRAPHITE The burn rate is 1 in/min (25 mm/min) based on ASTM FM VSS 302. Multi-Flex TPE contains Kratonâ„¢ G.Data provided by Multibase.
Tensile Strength, Ultimate	>= 3.62 MPa	>= 525 psi	ASTM D412
Multibase Multi-Flex® TPE A 6006 BLK Multi-Flex TPE contains Kraton™ G.Data provided by Multibase.
Tensile Strength, Ultimate	>= 3.62 MPa	>= 525 psi	ASTM D412
Multibase Multi-Flex® TPE A 6221 NAT The burn rate is 1 in/min (25 mm/min) based on ASTM FM VSS 302. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase.
Tensile Strength, Ultimate	>= 3.62 MPa	>= 525 psi	ASTM D412
Multibase Multi-Flex® TPE A 6421 BLK The burn rate is 1 in/min (25 mm/min) based on ASTM FM VSS 302. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase.