Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 400 MPa @Temperature 200 °C |
58000 psi @Temperature 392 °F |
EN min.; EN 10002-5 |
Outokumpu 4301 Cr-Ni Austenitic Stainless Steel General purpose steel with good corrosion resistance.Applications: Wide variety of applications in construction, chemical, petroleum, automobile, and domestic appliance markets.Available in hot roll.. |
|||
Tensile Strength, Ultimate | 400 MPa @Temperature 400 °C |
58000 psi @Temperature 752 °F |
EN min.; EN 10002-5 |
Outokumpu 4845 High Temperature Austenitic Stainless Steel Standardized high-temperature steel for use at temperatures up to 1100°C in dry air. Prone to embrittlement after exposure between 600-900°C. Applications: Heat and creep resistance. For use o.. |
|||
Tensile Strength, Ultimate | 400 MPa | 58000 psi | |
PSM Industries Pacific Sintered Metals High Carbon Copper Steel FCC-200-P Powdered Metal High strength, Good impact resistant material for mechanical components, Excellent hardenability, High performance material with high strength and wear resistance after heat treatment Equivalent MP.. |
|||
Tensile Strength, Ultimate | >= 400 MPa | >= 58000 psi | |
MetalTek C86400 Leaded Manganese Bronze High strength and hardness copper-zinc alloy.Applications: Steel mill nuts, ordnance parts, worm gears.Information provided by MetalTekCast UNS C86400; Cast Grade C86401; Cast ASTM B271, B584, B148;.. |
|||
Tensile Strength, Ultimate | 400 MPa @Diameter 12.7 mm |
58000 psi @Diameter 0.500 in |
|
Kaiser 6033 T8 Rod & Bar Alloy 6033 is a higher strength version of alloy 6061, approaching properties typically obtainable with 2000 series alloys. The alloy was developed to also offer improved machinability over 6061. Th.. |
|||
Tensile Strength, Ultimate | 400 MPa @Temperature 870 °C |
58000 psi @Temperature 1600 °F |
|
Haynes 214® alloy, cold rolled annealed sheet 2.0-3.2 mm thick Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Tensile Strength, Ultimate | 400 - 540 MPa | 58000 - 78300 psi | |
Materion Beryllium Copper Alloy M25 Wire; A (TB00) Temper; 1.3-12.7 mm Diameter (UNS C17300) Treatment required for max strength: as suppliedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed its name to.. |
|||
Tensile Strength, Ultimate | >= 400 MPa | >= 58000 psi | |
H.C. Starck WCu 75/25 Tungsten-Copper Composite Material Description of Product: Tungsten-copper composite materials are produced by copper infiltration of porous sintered tungsten. They are available with different copper contents (10 - 30 %). A therm.. |
|||
Tensile Strength, Ultimate | <= 400 MPa | <= 58000 psi | |
SSAB Tunnplat Domex® 200 Cold-forming Steel Cold-forming SteelCharacteristics: Domex® is specifically intended for deep-drawing operations. Due to its close tolerances and fine surfaces, hot-rolled Domex 200 can replace cold reduced deep-.. |
|||
Tensile Strength, Ultimate | >= 400 MPa | >= 58000 psi | |
Alcoa Excalibar® 6013-T8 Aluminum, 1.9-3.8 cm diameter Weldability = A; Stress Corrosion Cracking Resistance = A; General Corrosion Resistance = B (A = best; E = worst). General 6013 characteristics and uses: High strength and good corrosion resistance... |
|||
Tensile Strength, Ultimate | 400 - 503 MPa | 58000 - 73000 psi | |
Eagle Brass 510 Phosphor Bronzes 5% A, 1/2 Hard Alloy C510 is an alloy with good strength, formability and stress relaxation characteristics, and solderability. Applications include electronic parts, springs, switches, contacts and fasteners.Info.. |
|||
Tensile Strength, Ultimate | 400 - 496 MPa | 58000 - 72000 psi | |
Eagle Brass 706 Copper Nickel 10%, 1/2 Hard 706 exhibits excellent corrosion resistance, especially in marine applications. It has a relatively high strength and has resistance at elevated temperatures. The cost is relatively high compared to.. |
|||
Tensile Strength, Ultimate | 400 - 496 MPa | 58000 - 72000 psi | |
Eagle Brass 715 Copper Nickel 30%, 1/4 Hard 715 exhibits excellent corrosion resistance, especially in marine applications. It has moderately high strength and has good creep resistance at elevated temperatures. The cost is relatively high co.. |
|||
Tensile Strength, Ultimate | 400 - 496 MPa | 58000 - 72000 psi | |
Eagle Brass 752 Nickel Silver 18%, 1/4 Hard Alloy C752 combines corrosion resistance with strength and a lustrous silver color. Applications include optical frames and parts, springs, surgical instruments, jewelry, resistors and contacts.Info.. |
|||
Tensile Strength, Ultimate | <= 400 MPa | <= 58000 psi | |
CLAL-MSX ARCAP Anticorrosion AP1 0 Annealed, Rolled Copper Alloy Description: The AP1D grade has been developed especially for being machined by lathe. The very good machineability of the AP1D grade may be summerised by: cutting speed up to 150 m/minute (accordin.. |
|||
Tensile Strength, Ultimate | 400 MPa | 58000 psi | cold worked |
CMW® ELKONIUM 217 Silver Cadmium Alloy The alloying of silver with cadmium produces materials with good arc extinction, good corrosion resistance and low contact resistance characteristics and provides them with good switching capability.. |
|||
Tensile Strength, Ultimate | 400 MPa | 58000 psi | annealed |
CMW® ELKONIUM 76 gold based alloy Pure gold has complete resistance to atmospheric tarnish and oxidation. It does not contribute to polymer formations like platinum and palladium alloys. Wrought gold metal is very soft and prone to .. |
|||
Tensile Strength, Ultimate | 400 - 460 MPa | 58000 - 66700 psi | |
ArcelorMittal IF 300 High strength IF steel, Cold rolled Available in the following: Extragal®/Galvannealed (HX300YD+Z/+ZF)Description: These steels were designed to provide an excellent combination of drawability and mechanical strength based on their .. |
|||
Tensile Strength, Ultimate | >= 400 MPa | >= 58000 psi | |
AK Steel ASTM A 568 and A 635 Hot Rolled Carbon Steel, Structural Steel (SS) For conversion to A36 plateInformation provided by AK Steel |
|||
Tensile Strength, Ultimate | 400 MPa @Temperature 871 °C |
58000 psi @Temperature 1600 °F |
|
Haynes 230® alloy, cold rolled and 1232°C solution annealed sheet Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |