Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 2.30 MPa | 334 psi | ASTM D412 |
Multibase Multi-Flex® TPE A 7699 BLK Multi-Flex® A 7699 is an acoustic barrier compound for medium density applications . Multi-Flex® TPE compounds are based on Shell Kraton G polymers licensed to Multibase. Multi-Flex TPE contains.. |
|||
Tensile Strength, Ultimate | 2.30 MPa | 334 psi | ASTM D638-95 |
Multibase Multi-Pro® 2507 T NAT 25% Filler Content Polypropylene Moisture is less than 0.06%. Multi-Pro 2507 T Natural is designed for high impact and high flexural strength. It can easily be colored and is FDA approved.Data provided by Multibase. |
|||
Tensile Strength, Ultimate | 2.30 MPa | 334 psi | ISO 37 |
Multibase TPSiV® 4000-60A Thermoplastic Elastomer FEATURES & BENEFITS: Soft silky feel; Excellent abrasion and scratch resistance; Excellent bonding to PC, ABS; UV stableAPPLICATIONS: Solution for soft touch overmolding on consumer electronics, mob.. |
|||
Tensile Strength, Ultimate | 2.30 MPa | 334 psi | ASTM D 638 |
REXtac Rextac® RT 2115 Amorphous Polyalphaolefin (APAO) Adhesive and Sealant Grade.Description: Propylene homopolymer and FDA compliantFeatures: High softening point and short open timeApplications: Component of hot melt adhesives, sealants and specialty.. |
|||
Tensile Strength, Ultimate | 2.30 MPa | 334 psi | ASTM D638 |
ExxonMobil Escorene® MV-02520 EVA Copolymer, Adhesive and Sealant Grade
(discontinued **) Data provided by the manufacturer, Exxon Chemical.An experimental, very high flow, 20% vinyl acetate copolymerApplications: Hot melt adhesives; Wax blends; Industrial sealants. |
|||
Tensile Strength, Ultimate | 2.30 - 2.90 MPa | 334 - 421 psi | DIN 54 504 |
Dow BETAMATE™ 7200 Polyurethane Prepolymer BETAMATE™ 7200 is a one component moisture curing polyurethane seam sealant with permanent elasticity and good adhesion to different substrates. It is an excellent seam sealer for body repair. It.. |
|||
Tensile Strength, Ultimate | 2.30 - 2.90 MPa | 334 - 421 psi | DIN 54 504 |
Dow BETAMATE™ 7201 Polyurethane Prepolymer BETAMATE™ 7201 is a one component moisture curing polyurethane seam sealant with permanent elasticity and good adhesion to different substrates. It is an excellent seam sealer for body repair. It.. |
|||
Tensile Strength, Ultimate | 2.30 - 2.90 MPa | 334 - 421 psi | DIN 54 504 |
Dow BETAMATE™ 7205 Polyurethane Prepolymer BETAMATE™ 7205 is a one component moisture curing polyurethane seam sealant with permanent elasticity and good adhesion to different substrates. It is an excellent seam sealer for body repair. It.. |
|||
Tensile Strength, Ultimate | 2.30 MPa | 334 psi | 508 mm/min; ASTM D638 |
Dow Engage® ENR 7447.00 Ethylene-Butene Copolymer Description: ENR 7447.00 is a high flow, low density ethylene-butene copolymer designed for use in combination with our other elastomers to provide tailored solutions in polymer modification applica.. |
|||
Tensile Strength, Ultimate | 2.30 MPa | 334 psi | infiltrated with flexseal (8-dip process); ASTM D638 |
3D Systems DuraForm® Flex Thermoplastic Elastomer for SLS® Systems Thermoplastic elastomer material with rubber-like flexibility and functionality. For use with all selective laser sintering SLS® systems.ApplicationsAthletic footwear and equipmentGaskets, hoses an.. |