Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 27.5 MPa | 3990 psi | ASTM D638 |
Ineos G36-24-149 MDPE with Carbon Black
(discontinued **) Fortiflex® G36-24-149 is a black medium density polyethylene resin designed for sheet extrusion. This resin has excellent environmental stress crack resistance (ESCR) and ultra violet protection. .. |
|||
Tensile Strength, Ultimate | 27.5 MPa | 3990 psi | 2 in/min.; ASTM D638 |
Ineos G36-24-150 HDPE Ineos G36-24-150 is a medium density polyethylene resin designed for geomembrane sheet extrusion. The resin has excellent environmental stress crack resistance (ESCR).Natural resin; some physical p.. |
|||
Tensile Strength, Ultimate | 27.5 MPa | 3980 psi | ASTM D412 |
SK Chemicals SKYTHANE® 870A T series Polyurethane SKYTHANE is a thermoplastic polyurethane elastomer (TPU). Like materials ranging from rubber to plastics, it has excellent physical properties such as anti-abrasion, oil-resistance and mechanical pr.. |
|||
Tensile Strength, Ultimate | 27.5 MPa | 3980 psi | ASTM D412 |
SK Chemicals SKYTHANE® T870A Polyester Based, Low Hardness Thermoplastic Polyurethane Elastomer Description: SK Chemicals has supplied Thermoplastic Polyurethane Elastomer (TPU) under the name of SKYTHANE. Applications include:Keyboard CoversOutsoles of Soccer ShoesWire and CableAirbagsSheets .. |
|||
Tensile Strength, Ultimate | 27.5 MPa | 3980 psi | ASTM D412 |
Lubrizol Estane® T470A Thermoplastic Polyurethane Type: Estane® T470A is a Shore 77A, polyester grade, plasticizer-free, with low hardness thermoplastic polyurethane (TPU).Uses: Injection Molding, Extrusion.Availability: AsiaInformation Provided b.. |
|||
Tensile Strength, Ultimate | 27.5 MPa @Temperature 260 °C |
3990 psi @Temperature 500 °F |
ASTM D1708 |
Daelim H&L Plavis-G40 CM 40% Graphite Filled Aromatic Polyimide Bearing Compression Molded. Plavis-G-40: Graphite 40 wt% filled, Self lubricating grade with low thermal expansion.General Plavis information for all grades:PLAVIS polyimide has nitrogen bonded to 3 carbo.. |
|||
Tensile Strength, Ultimate | 27.5 MPa @Temperature 260 °C |
3990 psi @Temperature 500 °F |
ASTM D1708 |
Daelim H&L Plavis-G40 ISO 40% Graphite Filled Aromatic Polyimide Bearing Isostatically Molded. Plavis-G-40: Graphite 40 wt% filled, Self lubricating grade with low thermal expansion.General Plavis information for all grades:PLAVIS polyimide has nitrogen bonded to 3 car.. |
|||
Tensile Strength, Ultimate | 27.5 MPa @Thickness 1.14 - 1.52 mm, Temperature 704 °C |
3990 psi @Thickness 0.0449 - 0.0598 in, Temperature 1300 °F |
|
AK Steel 409 Ferritic Stainless steel AK Steel 409 Stainless Steels are especially useful for applications where oxidation or corrosion protection beyond the capacity of carbon steel and some coated steels is needed. Current applicatio.. |
|||
Tensile Strength, Ultimate | 27.5 - 52.5 MPa @Temperature 130 - 175 °C |
3990 - 7610 psi @Temperature 266 - 347 °F |
Average value: 70.7 MPa Grade Count:2 |
Overview of materials for Nylon 6, 10% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 10% Glass Fiber Filled". Specific grades with glass content between 5% and 14% are included. .. |
|||
Tensile Strength, Ultimate | 27.5 - 52.5 MPa @Time 1.80e+7 - 7.20e+7 sec |
3990 - 7610 psi @Time 5000 - 20000 hour |
Average value: 70.7 MPa Grade Count:2 |
Overview of materials for Nylon 6, 10% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 10% Glass Fiber Filled". Specific grades with glass content between 5% and 14% are included. .. |