Polymer Property : Tensile Strength, Ultimate = 189000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	1303 MPa @Treatment Temp. 593 Â°C, Time 1.44e+7 sec	189000 psi @Treatment Temp. 1100 Â°F, Time 4000 hour	Room temp test after thermal exposure
Haynes HastelloyÂ® C-22HSâ„¢ Nickel Alloy Plate, Age-hardened Outstanding Corrosion Resistance, High Strength HASTELLOYÂ® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou..
Tensile Strength, Ultimate	1300 MPa	189000 psi
Special Metals INCONELÂ® 706 Precipitation Hardening Alloy, Cold Rolled Sheet, 3 Part Heat Treatment, 0.062 inch (1.57 mm) Thickness Tensile and bearing strengths (ultimate and yield) and elongation values reported here are typical for Cold Rolled Sheet, 3 Part Heat Treatment, 0.062 inch (1.57 mm) Thickness samples. Density and m..
Tensile Strength, Ultimate	1300 MPa	189000 psi
Special Metals INCONELÂ® 706 Precipitation Hardening Alloy, Hot Finished Rod, 3 Part Heat Treatment, 8.0 inch (203 mm) Diameter Tensile strength (ultimate and yield), compressive strength, reduction of area, and elongation values reported here are typical for Hot Finished Rod, 3 Part Heat Treatment, 8.0 inch (203 mm) Diamete..
Tensile Strength, Ultimate	1300 MPa	189000 psi	Typical
TIMET TIMETAL® 15-3 Titanium Alloy (Ti-15V-3Cr-3Sn-3Al); Aged at 482°C High-Strength, Cold Formable Strip AlloyIndustry Specifications: USA Aerospace: AMS 4914A.Features: Cold formable and weldable, this strip alloy is primarily used for aircraft ducting, pressure vess..
Tensile Strength, Ultimate	1300 MPa @Temperature 20.0 °C	189000 psi @Temperature 68.0 °F	Longitudinal Tests from 6.3" rolled plate at 375 HB
EDRO EDRO400™ #40 Prehardened Insert Quality Martensitic Stainless Steel EDRO400™ is a remelted 400 series martensitic stainless steel supplied prehardened to 40 HRC (375 HB).EDRO400™ is characterized by excellent polishability, superior corrosion resistance, high leve..
Tensile Strength, Ultimate	1300 MPa	189000 psi	Double Age
Crucible Compaction Metals P/M 625M Corrosion Resistant Alloy P/M 625M (chemically, UNS N07626) is produced by the state-of-the-art Crucible P/M process: inert gas atomization, coupled with consolidation by hot isostatic pressing (HIP) and/or extrusion. The a..
Tensile Strength, Ultimate	1300 MPa	189000 psi	Hardened 1800°F, Tempered 800°F
ATI Allegheny Ludlum 410 Martensitic Stainless Steel Characteristics: superior wear resistance, hardenable, excellent corrosion resistance. Applications:cutlery, dental and surgical instruments, nozzles, valve parts, hardened steel ball and seats for..
Tensile Strength, Ultimate	1300 MPa	189000 psi	Typical
ATI Allegheny Ludlum Martensitic Stainless Steel Type 410, Hardened + 427°C Temper Allegheny Ludlum Type 410 is a hardenable straight-chromium stainless steel which combines superior wear resistance of high carbon alloys with the excellent corrosion resistance of chromium stainles..