TIMET TIMETAL® 15-3 Titanium Alloy (Ti-15V-3Cr-3Sn-3Al); Aged at 482°C
| Category | Metal , Nonferrous Metal , Titanium Alloy , Beta Titanium Alloy |
| Manufacturer | TIMET |
| Trade Name | TIMETAL® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | TIMET TIMETAL® 15-3 Titanium Alloy (Ti-15V-3Cr-3Sn-3Al); Aged at 482°C.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High-Strength, Cold Formable Strip AlloyIndustry Specifications: USA Aerospace: AMS 4914A.Features: Cold formable and weldable, this strip alloy is primarily used for aircraft ducting, pressure vessels and other fabricated sheet metal structures up to 300°C.Typical heat treatment for this alloy: Solution Treatment: 790°C for 3-20 min, air cool. Age Treatment: 480-620°C for 4-16 hrs.Data provided by TIMET.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 4.78 g/cc | 0.173 lb/in³ | Typical |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 1300 MPa | 189000 psi | Typical |
| Tensile Strength, Yield | 1210 MPa @Strain 0.200 % |
175000 psi @Strain 0.200 % |
Typical |
| Elongation at Break | 9.0 % | 9.0 % | Typical |
| Modulus of Elasticity | 107 GPa | 15500 ksi | Typical |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 8.60 µm/m-°C @Temperature 20.0 °C |
4.78 µin/in-°F @Temperature 68.0 °F |
|
| 9.20 µm/m-°C @Temperature 20.0 - 250 °C |
5.11 µin/in-°F @Temperature 68.0 - 482 °F |
||
| 9.90 µm/m-°C @Temperature 20.0 - 500 °C |
5.50 µin/in-°F @Temperature 68.0 - 932 °F |
||
| Specific Heat Capacity | 0.500 J/g-°C | 0.120 BTU/lb-°F | |
| Thermal Conductivity | 8.30 W/m-K | 57.6 BTU-in/hr-ft²-°F | |
| Maximum Service Temperature, Air | 288 °C | 550 °F | |
| Beta Transus | 760 °C | 1400 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Aluminum, Al | 2.5 - 3.5 % | 2.5 - 3.5 % | |
| Carbon, C | <= 0.050 % | <= 0.050 % | |
| Chromium, Cr | 2.5 - 3.5 % | 2.5 - 3.5 % | |
| Hydrogen, H | <= 0.015 % | <= 0.015 % | |
| Iron, Fe | <= 0.25 % | <= 0.25 % | |
| Nitrogen, N | <= 0.050 % | <= 0.050 % | |
| Oxygen, O | <= 0.13 % | <= 0.13 % | |
| Tin, Sn | 2.5 - 3.5 % | 2.5 - 3.5 % | |
| Titanium, Ti | 72.6 - 78.5 % | 72.6 - 78.5 % | Calculated as remainder |
| Vanadium, V | 14 - 16 % | 14 - 16 % |