Polymer Property : Tensile Strength, Ultimate = 1410 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English
Tensile Strength, Ultimate	1410 - 1420 MPa	205000 - 206000 psi
Latrobe LescalloyÂ® UT-18 VAC-ARC ; 3.25 in. round High Strength Alloy Steel UT-18 VAC-ARC is a medium-carbon, low-alloy heat resistant steel having high strength to 1000Â°F. It is used primarily for turbine and compressor rotor shafts. Vacuum consumable electrode melting..
Tensile Strength, Ultimate	1410 - 1420 MPa	204000 - 206000 psi
Latrobe LescalloyÂ® UT-18 VAC-ARC ; 4 in. round High Strength Alloy Steel UT-18 VAC-ARC is a medium-carbon, low-alloy heat resistant steel having high strength to 1000Â°F. It is used primarily for turbine and compressor rotor shafts. Vacuum consumable electrode melting..
Tensile Strength, Ultimate	1410 MPa	205000 psi
Latrobe LescalloyÂ® UT-18 VAC-ARC ; 6 in. round High Strength Alloy Steel UT-18 VAC-ARC is a medium-carbon, low-alloy heat resistant steel having high strength to 1000Â°F. It is used primarily for turbine and compressor rotor shafts. Vacuum consumable electrode melting..
Tensile Strength, Ultimate	1410 MPa	205000 psi
Haynes 556Â® alloy, 50% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Tensile Strength, Ultimate	>= 1410 MPa	>= 205000 psi
Materion Nibryl Beryllium Nickel Alloy (Nibryl)-360 Rod and Bar; H1050 (H1050) Temper; All Sizes (UNS N03360) Tabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed its name to Materion Corporation in March 2011.
Tensile Strength, Ultimate	1410 - 1420 MPa	204000 - 206000 psi
Latrobe Lescalloy® UT-18 VAC-ARC ; 1.75 in. round High Strength Alloy Steel UT-18 VAC-ARC is a medium-carbon, low-alloy heat resistant steel having high strength to 1000°F. It is used primarily for turbine and compressor rotor shafts. Vacuum consumable electrode melting i..