Polymer Property : Tensile Strength, Ultimate = 136000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	820 - 940 MPa	119000 - 136000 psi
Materion Beryllium Copper Alloy 190 Strip; 1/2HM (TM02) Temper (UNS C17200) Treatment required for max strength: Mill HardenedStress Relaxation-% Stress Remaining after 1000 hrs @ 100Â°C: 97%Stress Relaxation after 1000 hrs @ 200Â°C: 67%Formability Ratio, 90Â° Bend, R..
Tensile Strength, Ultimate	750 - 940 MPa	109000 - 136000 psi
Materion Beryllium Copper Alloy 25 Wire; 1/2H (TD02) Temper; 1.3-12.7 mm Diameter (UNS C17200) Treatment required for max strength: as suppliedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed its name to..
Tensile Strength, Ultimate	750 - 940 MPa	109000 - 136000 psi
Materion Beryllium Copper Alloy M25 Wire; 1/2H (TD02) Temper; 1.3-12.7 mm Diameter (UNS C17300) Treatment required for max strength: as suppliedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed its name to..
Tensile Strength, Ultimate	790 - 940 MPa	115000 - 136000 psi	Guaranteed, 1/4 t
Industeel SUPERELSOÂ® 690CR Quenched and Tempered High Strength Steel for Leg Components of Jack-up Rigs SuperelsoÂ® 690 CR (SE 690 CR) is a 690MPa (100ksi) yield strength quenched and tempered steel adapted for jack-up rig legs of offshore drilling platforms. SuperelsoÂ® 690 CR is manufactured via..
Tensile Strength, Ultimate	770 - 940 MPa	112000 - 136000 psi
Industeel SUPRALSIMÂ® 690 HLE Steel for Welded and Weight-Saving Structures Description: SUPRALSIMÂ® 690 is general steel plate for structure enables to make weight savings thanks to a minimum yield strength of 690 N/mmÂ². Thanks to its exceptional purity rate (very low..
Tensile Strength, Ultimate	750 - 940 MPa	109000 - 136000 psi
Materion Beryllium Copper Alloy 3 Strip; HT (TH04) Temper (UNS C17510) Treatment required for max strength: 2-3 hrs @ 480ºC or Mill HardenedStress Relaxation-% Stress Remaining after 1000 hrs @ 100°C: 96%Stress Relaxation after 1000 hrs @ 200°C: 75%Formability Ratio..