Polymer Property : Tensile Strength, Ultimate = 119000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	820 - 940 MPa	119000 - 136000 psi
Materion Beryllium Copper Alloy 190 Strip; 1/2HM (TM02) Temper (UNS C17200) Treatment required for max strength: Mill HardenedStress Relaxation-% Stress Remaining after 1000 hrs @ 100Â°C: 97%Stress Relaxation after 1000 hrs @ 200Â°C: 67%Formability Ratio, 90Â° Bend, R..
Tensile Strength, Ultimate	>= 820 MPa	>= 119000 psi
Materion BrushformÂ® 290 Beryllium Copper Alloy Strip; TM02 Temper (UNS C17200) Treatment required for max strength: Mill HardenedStress Relaxation-% Stress Remaining after 1000 hrs @ 100Â°C: 97%Stress Relaxation after 1000 hrs @ 200Â°C: 76%Formability Ratio, 90Â° Bend, R..
Tensile Strength, Ultimate	821 MPa	119000 psi
Haynes HastelloyÂ® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged at 649Â°C (1200Â°F) for 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093Â°C, good high temperature and thermal fatigue strength. Application..
Tensile Strength, Ultimate	820 MPa	119000 psi
Haynes 556Â® alloy, sheet after 1000 hours at 760Â°C (1400Â°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Tensile Strength, Ultimate	822 MPa	119000 psi	No thermal exposure
Haynes HastelloyÂ® C-22HSâ„¢ Nickel Alloy Plate, Annealed Outstanding Corrosion Resistance, High Strength HASTELLOYÂ® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou..
Tensile Strength, Ultimate	821 MPa @Treatment Temp. 427 Â°C, Time 1.44e+7 sec	119000 psi @Treatment Temp. 801 Â°F, Time 4000 hour	Room temp test after thermal exposure
Haynes HastelloyÂ® C-22HSâ„¢ Nickel Alloy Plate, Annealed Outstanding Corrosion Resistance, High Strength HASTELLOYÂ® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou..
Tensile Strength, Ultimate	818 MPa	119000 psi
Haynes HastelloyÂ® C-4 alloy, welded plate 12.7 mm (1/2 in.) thick, aged 1000 hours at 649Â°C (1200Â°F) Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900Â°F (649 to 1038Â°C) rang..
Tensile Strength, Ultimate	820 MPa @Temperature 538 °C	119000 psi @Temperature 1000 °F
Crucible Steel 15-5 Precipitation Hardening Stainless Steel Crucible 15-5 is a Premium Quality precipitation-hardening stainless steel which is capable of high strength and hardness levels after a relatively simple heat-treatment procedure. This grade is a V..
Tensile Strength, Ultimate	820 MPa @Temperature 538 °C	119000 psi @Temperature 1000 °F
Crucible Steel 17Cr-4Ni Precipitation Hardening Stainless Steel Crucible 17Cr-4Ni is a precipitation-hardening stainless steel which is capable of a high strength and hardness levels after a relatively simple heat-treatment procedure. This grade is martensitic a..
Tensile Strength, Ultimate	820 MPa @Temperature 538 °C	119000 psi @Temperature 1000 °F
Crucible Steel 17Cr-4Ni Super-X® Precipitation Hardening Stainless Steel Crucible 17Cr-4Ni is a version of 17CR-4Ni which has been modified to substantially improve machinability and other properties. Patented 17Cr-4Ni Super-X meets industry specifications for 17Cr-4Ni. ..
Tensile Strength, Ultimate	>= 820 MPa	>= 119000 psi	Wire
CLAL-MSX ARCAP Anticorrosion AP1C H15 Spring, Drawn Copper Alloy Description: The AP1C grade (used in rods for parts that are to be deformed by torsion, bending, riveting, swaging... and for welding) and the AP1 grade (sheet, strip, wire, tubes) is machineable un..
Tensile Strength, Ultimate	819 MPa @Temperature -78.0 °C	119000 psi @Temperature -108 °F
ATI Allegheny Ludlum Altemp® HX Nickel-Based superalloy Characteristics: outstanding resistance to oxidation at high temperatures, exceptional strength at elevated temperatures, good fabricability, good machinability in annealed condition, work hardening..
Tensile Strength, Ultimate	818 MPa	119000 psi
ATI Allegheny Ludlum Stainless Steel Type 439/AL 439HP™, 70% cold work (ASTM XM-8; UNS S43035) Allegheny Ludlum Stainless Steel Type 439, a titanium stabilized, 18 percent chromium alloy, also known as ASTM XM-8 and by the UNS designation S43035, is a ferritic stainless steel designed to resi..
Tensile Strength, Ultimate	820 MPa	119000 psi
Haynes Hastelloy® alloy 625 12.7 mm plate weldments Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica..