Polymer Property : Tensile Strength, Ultimate = 136000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	938 MPa @Temperature 400 Â°C	136000 psi @Temperature 752 Â°F
Kennametal Stellite NucalloyÂ® 488 High-Silicon Nickel-Base Hardfacing Alloy NucalloyÂ® alloys are unique, patented, high-silicon, nickel-base hardfacing alloys that are designed to have optimum combinations of hardness and toughness, similar to the cobalt base alloys . B..
Tensile Strength, Ultimate	935 MPa	136000 psi
Kennametal Stellite StelliteÂ® 6B solution heat-treated at 1232Â°C, air cooled, 15.9 mm thick plate Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and..
Tensile Strength, Ultimate	935 MPa	136000 psi
Haynes 214Â® alloy, sheet, 100 hours exposure at 870Â°C (1600Â°F) Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Tensile Strength, Ultimate	935 MPa	136000 psi
Haynes 230Â® alloy, 20% cold reduction, 1121Â°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149Â°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic..
Tensile Strength, Ultimate	936 MPa	136000 psi	Hardened 1900°F, Tempered 1200°F
ATI Allegheny Ludlum 425 Mod Martensitic Stainless Steel Characteristics: superior wear resistance, hardenable, excellent corrosion resistance. Applications:cutlery, dental and surgical instruments, nozzles, valve parts, hardened steel ball and seats for..
Tensile Strength, Ultimate	940 MPa	136000 psi
ATI Allegheny Ludlum AL 625HP™ Stainless Steel Nickel-based superalloy. Characteristics:exceptional fatigue resistance, excellent resistance to oxidation and corrosion, outstanding strength and toughness over a range of temperatures from cryogen..
Tensile Strength, Ultimate	938 MPa	136000 psi	Longitudinal
AK Steel 15-5 PH® Precipitation Hardening Stainless Steel, Condition H 1150-M AK Steel 15-5 PH® provides high strength, good corrosion resistance, good mechanical properties at temperatures up to 600°F (316°C), and good toughness in both base metal and welds. Short-time, ..
Tensile Strength, Ultimate	936 MPa	136000 psi	Typical
ATI Allegheny Ludlum Martensitic Stainless Steel Type 425 Mod, Hardened + 649°C (1200°F) Temper Allegheny Ludlum Type 425 Mod is a hardenable straight-chromium stainless steel which combines superior wear resistance of high carbon alloys with the excellent corrosion resistance of chromium stai..
Tensile Strength, Ultimate	940 - 1100 MPa	136000 - 160000 psi	Typical
Industeel SUPERELSO® 890 HLE Steel for Welded and Weight-Saving Structures Description: SUPERELSO® 890 is quenched and tempered steel for structure with higher strength. Thanks to a minimum yield strength of 890 N/mm² (130 KSI), SUPERELSO® 890 enables to make weight sav..
Tensile Strength, Ultimate	940 MPa	136000 psi
Kennametal Stellite Stellite® 4 Cobalt Chromium Alloy The higher tungsten content of Stellite alloy 4 gives improved high temperature properties and an increase in abrasive wear resistance over Stellite alloy 6, but not as good as Stellite alloy 12 or ..