Polymer Property : Tensile Strength, Ultimate = 94300 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English
Tensile Strength, Ultimate	650 MPa @Temperature 760 Â°C	94300 psi @Temperature 1400 Â°F
Haynes X-750 Nickel Alloy Sheet and Strip (AMS 5598, UNS N07750) Haynes X-750 (UNS No. N07750) alloy is an age-hardenable, nickel-base superalloy with very good strength at temperatures up to about 1600Â°F (870Â°C). It is widely used as a wrought material for..
Tensile Strength, Ultimate	650.2 MPa @Thickness 2.00 mm, Temperature 427 Â°C	94300 psi @Thickness 0.0787 in, Temperature 801 Â°F
Haynes HastelloyÂ® C-276 alloy, solution heat treated flat products HastelloyÂ® C-276 alloy is a nickel-molybdenum-chromium wrought alloy that is a versatile corrosion-resistant alloy. C-276 alloy is an improved wrought version of alloy C in that it usually doesn'..
Tensile Strength, Ultimate	650.2 MPa @Thickness 4.80 - 25.4 mm, Temperature 316 Â°C	94300 psi @Thickness 0.189 - 1.00 in, Temperature 601 Â°F
Haynes HastelloyÂ® C-276 alloy, solution heat treated flat products HastelloyÂ® C-276 alloy is a nickel-molybdenum-chromium wrought alloy that is a versatile corrosion-resistant alloy. C-276 alloy is an improved wrought version of alloy C in that it usually doesn'..
Tensile Strength, Ultimate	650 MPa @Temperature 20.0 °C	94300 psi @Temperature 68.0 °F
CRP Technology AMC225xe Aluminum Alloy - SiC Composite, T4 Condition AMC225xe is a high quality aerospace grade aluminum alloy (AA2124) reinforced with 25% by volume of ultrafine particles of silicon carbide. It is manufactured by a special powder metallurgy route us..