Polymer Property : Tensile Strength, Ultimate = 103000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 712 MPa

@Thickness 25.4 mm,
Temperature 371 °C
 103000 psi

@Thickness 1.00 in,
Temperature 700 °F
Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Bar, Hot Rolled and Solution Annealed
HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing..
Tensile Strength, Ultimate 712 MPa

@Thickness 12.7 mm,
Temperature 260 °C
 103000 psi

@Thickness 0.500 in,
Temperature 500 °F
Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Shielded Metal Arc Welded (SMAW) Plate
HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing..
Tensile Strength, Ultimate 708 MPa

@Diameter 12.7 mm,
Temperature 25.0 °C
 103000 psi

@Diameter 0.500 in,
Temperature 77.0 °F
 As welded
Haynes Hastelloy® C-22HS™ Nickel Alloy Gas Tungsten Arc Welded (GTAW) All Weld Cruciform
Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou..
Tensile Strength, Ultimate 707 MPa

@Thickness 12.7 mm,
Temperature 316 °C
 103000 psi

@Thickness 0.500 in,
Temperature 601 °F
Haynes Hastelloy® C-4 alloy, plate, heat treated at 1066°C, rapid quenched
Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) rang..
Tensile Strength, Ultimate 712 MPa

@Thickness 6.30 mm,
Temperature 316 °C
 103000 psi

@Thickness 0.248 in,
Temperature 601 °F
Haynes Hastelloy® C-4 alloy, plate, heat treated at 1066°C, rapid quenched
Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) rang..
Tensile Strength, Ultimate 710 MPa

@Temperature 23.0 °C
 103000 psi

@Temperature 73.4 °F
Special Metals INCONEL® Alloy 617
A nickel-chromium-cobalt-molybdenum alloy with an exceptional combination of metallurgical stability, strength, and oxidation resistance at high temperatures. Resistance to oxidation is enhanced by..
Tensile Strength, Ultimate 712 MPa

@Thickness 3.20 mm,
Temperature 204 °C
 103000 psi

@Thickness 0.126 in,
Temperature 399 °F
Haynes Hastelloy® C-4 alloy, sheet, aged 100 hours at 899°C
Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. T..
Tensile Strength, Ultimate 709 MPa

@Thickness 12.7 mm,
Temperature 316 °C
 103000 psi

@Thickness 0.500 in,
Temperature 601 °F
Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) Plate
HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing spe..
Tensile Strength, Ultimate 710 MPa

@Thickness 25.4 mm,
Temperature 25.0 °C
 103000 psi

@Thickness 1.00 in,
Temperature 77.0 °F
Haynes Hastelloy® G-35® Nickel Alloy Bar, Annealed at 2075°F (1135°C)
Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process” phosphoric acid, which is widely used in the production of fertilizers. Tests indicate that it is..